Direct synthesis of Ce0.8Sm0.2−xZnxO2−δ electrolyte by sol–gel for IT-SOFC
Yan Liu,Haobiao Qin,Meilin Li,Jinqun Cheng,Chunbao Tang,Jie Xiao,Yongmin Xie
DOI: https://doi.org/10.1007/s11581-022-04677-2
IF: 2.961
2022-09-21
Ionics
Abstract:In this paper, high-quality nanosized Ce 0.8 Sm 0.2− x Zn x O 2− δ ( x = 0, 0.02, 0.04, 0.08, and 0.16) powders are successfully synthesized by sol–gel process for intermediate-temperature solid oxide fuel cell (IT-SOFC) application. The thermal behavior, porosity, crystal phase, surface microstructure, and electrical properties of Ce 0.8 Sm 0.2− x Zn x O 2− δ are studied by thermogravimetric-differential scanning calorimeter (TG-DSC), Archimedes drainage method, X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical impedance spectroscopy (EIS), respectively. The results show that Ce 0.8 Sm 0.2− x Zn x O 2− δ electrolyte appears very high sintering activity even at sintering temperature as low as 1300 °C. The crystal phase of sample powders after sintered at 600 °C belongs to single-phase cubic fluorite structure with mean particle size of 15 nm. The lattice parameter increases first until doping 2 mol.% Zn and then decreases with more doping amount. Electrochemical performance results demonstrate that doping with appropriate amount of Zn can significantly improve the conductivity of SDC materials. The highest conductivity of 0.057 S·cm −1 at 800 °C is obtained for Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ , owing to high density, ultrafine grains, and increased grain boundaries. Furthermore, the fuel cell performance of Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ electrolyte is measured with 5 wt.% Fe-loaded activated carbon as the fuel. It delivers an outstanding performance, with an OCV of 1.02 V, a maximum power output of 408 mW·cm −2 at 850 °C, indicating that Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ may have potential application for IT-SOFC electrolyte materials.
chemistry, physical,physics, condensed matter,electrochemistry