Abstract:In this paper, high-quality nanosized Ce 0.8 Sm 0.2− x Zn x O 2− δ ( x = 0, 0.02, 0.04, 0.08, and 0.16) powders are successfully synthesized by sol–gel process for intermediate-temperature solid oxide fuel cell (IT-SOFC) application. The thermal behavior, porosity, crystal phase, surface microstructure, and electrical properties of Ce 0.8 Sm 0.2− x Zn x O 2− δ are studied by thermogravimetric-differential scanning calorimeter (TG-DSC), Archimedes drainage method, X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical impedance spectroscopy (EIS), respectively. The results show that Ce 0.8 Sm 0.2− x Zn x O 2− δ electrolyte appears very high sintering activity even at sintering temperature as low as 1300 °C. The crystal phase of sample powders after sintered at 600 °C belongs to single-phase cubic fluorite structure with mean particle size of 15 nm. The lattice parameter increases first until doping 2 mol.% Zn and then decreases with more doping amount. Electrochemical performance results demonstrate that doping with appropriate amount of Zn can significantly improve the conductivity of SDC materials. The highest conductivity of 0.057 S·cm −1 at 800 °C is obtained for Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ , owing to high density, ultrafine grains, and increased grain boundaries. Furthermore, the fuel cell performance of Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ electrolyte is measured with 5 wt.% Fe-loaded activated carbon as the fuel. It delivers an outstanding performance, with an OCV of 1.02 V, a maximum power output of 408 mW·cm −2 at 850 °C, indicating that Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ may have potential application for IT-SOFC electrolyte materials.

Conductivity Of Yttria-Doped Ceria Electrolyte Made By Chemical Coprecipitation And Its Evaluation For Sofc Application

YSZ Thin Films Prepared by a Novel Powder Coating Process on Porous NiO-YSZ Cermet

Enhancement of Conductivity in Phase Pure and Doped Ceria for Fuel Cell Applications

Preparation and Properties of Ce0.8Y0.2O1.9 Electrolyte

Synthesis and Characterization of (gd, Y)-Doped Ceria Electrolytes for Solid Oxide Fuel Cell

Electrical properties of CeO2-Y2O3 electrolyte SOFCs

High Performance Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Cobalt-free Sr0.7Y0.3CuO2+δ As a Cathode for Intermediate-Temperature Solid Oxide Fuel Cell

High Performance Low-Temperature Solid Oxide Fuel Cells Based on Nanostructured Ceria-Based Electrolyte

Fabrication and Characterizations of Ysz Electrolyte Films for Sofc

Preparation and Properties of Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Fabrication and Characterization of Composite Electrolyte for Intermediate-Temperature SOFC

Direct synthesis of Ce0.8Sm0.2−xZnxO2−δ electrolyte by sol–gel for IT-SOFC

Solid oxide fuel cell with a spin-coated yttria stabilized zirconia/gadolinia doped ceria bi-layer electrolyte

Fabrication, Microstructure and Properties of A Ysz Electrolyte for Sofcs

Development of Novel Low-Temperature SOFCs with Co-Ionic Conducting SDC-carbonate Composite Electrolytes

Fabrication of YSZ/SNDC Bilayer Electrolytes by Spark Plasma Sintering

High-performing and stable non-doped ceria electrolyte with amorphous carbonate coating layer for low-temperature solid oxide fuel cells

Preparation and characterization of nanocrystalline Ce0.8Sm0.2O1.9 for low temperature solid oxide fuel cells based on composite electrolyte

A Novel Gd3+ and Yb3+ Co-Doped Ceria-Sulphate Composite Electrolyte for Intermediate-Temperature Fuel Cells

Low Temperature Deposited (ce,gd)o2−x Interlayer for La0.6Sr0.4Co0.2Fe0.8O3 Cathode Based Solid Oxide Fuel Cell