Abstract:Application of anode-supported solid oxide fuel cell (SOFC) with ceria based electrolyte has often been limited by high cost of electrolyte film fabrication and high electrode polarization. In this study, dense Gd0.1Ce0.9O2 (GDC) thin film electrolytes have been fabricated on hierarchically oriented macroporous NiO-GDC anodes by a combination of freeze-drying tape-casting of the NiO-GDC anode, drop-coating GDC slurry on NiO-GDC anode, and co-firing the electrolyte/anode bilayers. Using 3D X-ray microscopy and subsequent analysis, it has been determined that the NiO-GDC anode substrates have a porosity of around 42% and channel size from around 10 μm at the electrolyte side to around 20 μm at the other side of the NiO-GDC (away from the electrolyte), indicating a hierarchically oriented macroporous NiO-GDC microstructure. Such NiO-GDC microstructure shows a tortuosity factor of ∼1.3 along the thickness direction, expecting to facilitate gas diffusion in the anode during fuel cell operation. SOFCs with such Ni-GDC anode, GDC film (30 μm) electrolyte, and La0.6Sr0.4Co0.2Fe0.8O3-GDC (LSCF-GDC) cathode show significantly enhanced cell power output of 1.021 W cm(-2) at 600 °C using H2 as fuel and ambient air as oxidant. Electrochemical Impedance Spectroscopy (EIS) analysis indicates a decrease in both activation and concentration polarizations. This study has demonstrated that freeze-drying tape-casting is a very promising approach to fabricate hierarchically oriented porous substrate for SOFC and other applications.

Boosting intermediate temperature performance of solid oxide fuel cells via a tri‐layer ceria–zirconia–ceria electrolyte

A simple and easy one-step fabrication of thin BaZr0.1Ce0.7Y0.2O3−δ electrolyte membrane for solid oxide fuel cells

A high performance intermediate temperature fuel cell based on a thick oxide–carbonate electrolyte

Scalable and facile fabrication of tri-layer electrolytes by reactive sputtering for efficient and durable solid oxide fuel cells

Highly dense and ultrathin gadolinia-doped ceria interlayer for enhanced performance of large-area anode-supported solid oxide fuel cell

Hierarchically oriented macroporous anode-supported solid oxide fuel cell with thin ceria electrolyte film.

Low Temperature Deposited (ce,gd)o2−x Interlayer for La0.6Sr0.4Co0.2Fe0.8O3 Cathode Based Solid Oxide Fuel Cell

Construction and Scale-Up of High Performing SOFC with Enhanced GdxCe1−xO2−δ Barrier Layer Self-Crystallization and Defect-Free GDC-YSZ Interface

Optimization of ScSZ/GDC bilayer thin film electrolyte for anodic aluminum oxide supported low temperature solid oxide fuel cells

Solid oxide fuel cell with a spin-coated yttria stabilized zirconia/gadolinia doped ceria bi-layer electrolyte

Sputter-deposited medium-temperature solid oxide fuel cells with multi-layer electrolytes

High Performance Solid Oxide Fuel Cells Based on Tri-Layer Yttria-Stabilized Zirconia by Low Temperature Sintering Process

Doped Zirconia/Ceria Electrolyte Fabricated at Low Temperature

Development of a new ceria/yttria-ceria double-doped bismuth oxide bilayer electrolyte low-temperature SOFC with higher stability

High Performance Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Low Temperature Solid Oxide Fuel Cells with Hierarchically Porous Cathode Nano-Network

Optimizing Bilayer Electrolyte Thickness Ratios for High-Performing Low-Temperature Solid Oxide Fuel Cells

High Performance Low-Temperature Solid Oxide Fuel Cells Based on Nanostructured Ceria-Based Electrolyte

Performance of a double-layer CGO/YSZ electrolyte for solid oxide fuel cells

Efficient strategy to boost the electrochemical performance of yttrium stabilized zirconia electrolyte solid oxide fuel cell for low-temperature applications

A cathode-supported SOFC with thin Ce0.8Sm0.2O1.9 electrolyte prepared by a suspension spray