Abstract:In this paper, high-quality nanosized Ce 0.8 Sm 0.2− x Zn x O 2− δ ( x = 0, 0.02, 0.04, 0.08, and 0.16) powders are successfully synthesized by sol–gel process for intermediate-temperature solid oxide fuel cell (IT-SOFC) application. The thermal behavior, porosity, crystal phase, surface microstructure, and electrical properties of Ce 0.8 Sm 0.2− x Zn x O 2− δ are studied by thermogravimetric-differential scanning calorimeter (TG-DSC), Archimedes drainage method, X-ray diffraction (XRD), scanning electron microscope (SEM), and electrochemical impedance spectroscopy (EIS), respectively. The results show that Ce 0.8 Sm 0.2− x Zn x O 2− δ electrolyte appears very high sintering activity even at sintering temperature as low as 1300 °C. The crystal phase of sample powders after sintered at 600 °C belongs to single-phase cubic fluorite structure with mean particle size of 15 nm. The lattice parameter increases first until doping 2 mol.% Zn and then decreases with more doping amount. Electrochemical performance results demonstrate that doping with appropriate amount of Zn can significantly improve the conductivity of SDC materials. The highest conductivity of 0.057 S·cm −1 at 800 °C is obtained for Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ , owing to high density, ultrafine grains, and increased grain boundaries. Furthermore, the fuel cell performance of Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ electrolyte is measured with 5 wt.% Fe-loaded activated carbon as the fuel. It delivers an outstanding performance, with an OCV of 1.02 V, a maximum power output of 408 mW·cm −2 at 850 °C, indicating that Ce 0.8 Sm 0.16 Zn 0.04 O 2− δ may have potential application for IT-SOFC electrolyte materials.

A high performance intermediate temperature fuel cell based on a thick oxide–carbonate electrolyte

Performance of fuel cells with proton-conducting ceria-based composite electrolyte and nickel-based electrodes

High Performance Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

Boosting intermediate temperature performance of solid oxide fuel cells via a tri‐layer ceria–zirconia–ceria electrolyte

High Performance Low-Temperature Solid Oxide Fuel Cells Based on Nanostructured Ceria-Based Electrolyte

Intermediate Temperature Fuel Cell Performance of the Composite Electrolyte Ce0.8Gd0.2O2-α-(Li/K)2CO3

A Novel Gd3+ and Yb3+ Co-Doped Ceria-Sulphate Composite Electrolyte for Intermediate-Temperature Fuel Cells

Preparation and Properties of Gd3+ and Y3+ Co-Doped Ceria-Based Electrolytes for Intermediate Temperature Solid Oxide Fuel Cells

A high-performance ceramic fuel cell with samarium doped ceria–carbonate composite electrolyte at low temperatures

Development of Novel Low-Temperature SOFCs with Co-Ionic Conducting SDC-carbonate Composite Electrolytes

Direct synthesis of Ce0.8Sm0.2−xZnxO2−δ electrolyte by sol–gel for IT-SOFC

Solid oxide fuel cell with a spin-coated yttria stabilized zirconia/gadolinia doped ceria bi-layer electrolyte

High-performing and stable non-doped ceria electrolyte with amorphous carbonate coating layer for low-temperature solid oxide fuel cells

Bifunctional Ce0.9Gd0.09M0.01O2−δ (M = Fe, Cu) interlayers with micro-doping for high-performance solid oxide fuel cells

Electrospun Core–Shell Fibers for High-Efficient Composite Cathode-Based Solid Oxide Fuel Cells

Interface channels accelerating ion transport through alkaline earth metal carbonate - Gd0.1Ce0.9O1.95 heterostructure

Fabrication and Characterization of Composite Electrolyte for Intermediate-Temperature SOFC

Sputter-deposited medium-temperature solid oxide fuel cells with multi-layer electrolytes

Development of a new ceria/yttria-ceria double-doped bismuth oxide bilayer electrolyte low-temperature SOFC with higher stability

Ceramic Fuel Cells Based on Ceria–carbonate Salt Composite Electrolyte

Synthesis and Characterization of (gd, Y)-Doped Ceria Electrolytes for Solid Oxide Fuel Cell