Advanced reaction-bonded SiC ceramics for space mirror blanks
P.S. Grinchuk,H.M. Abuhimd,M.V. Kiyashko,D.V. Solovei,A.V. Akulich,M.O. Stepkin,V.A. Lapitskaya,T.A. Kuznetsova,S.M. Danilova-Tretiak,L.E. Evseeva
DOI: https://doi.org/10.1016/j.jmapro.2024.01.069
IF: 5.684
2024-02-02
Journal of Manufacturing Processes
Abstract:This paper describes the advanced technology of reaction-bonded silicon carbide (RB-SiC) fabrication. The technology is focused on the production of space mirror blanks. Four types of RB-SiC ceramics are produced with different volumetric SiC content in the range from 78 to 93 %. Compared with space-proven materials, the developed RB-SiC has enhanced physical properties (density ρ = 3.14 g/cm 3 , Young's modulus E = 430 GPa, thermal conductivity λ = 186 W/(m·K), specific heat C p = 620 J/(kg·K), coefficient of thermal expansion α = 2·10 −6 K −1 ). This provides high values of criteria ψ 1 = E/ρ , ψ 2 = λ/α and maximum value of generalized Maksutov's criterion ψ 3 = Eλ/αρC p , which represents an improved thermo-mechanical deformation stability to optical distortions. Microhardness H and fracture toughness K IC are determined by the nanoindentation method separately for SiC phase ( H ∼ 35 GPa, the values of K IC increases from 4.3 to 5.0 MPa·m 1/2 with the increase of SiC content in the produced ceramics) and Si phase ( H ∼ 12.5 GPa, K IC ∼ 2.5 MPa·m 1/2 ) in composite RB-SiC material. Flexural strength is 230–260 MPa for different RB-SiC types. As this material is suitable for space application, lightweight mirror blanks with a diameter of 20.5 cm and an areal density of 16.5 kg/m 2 were produced to demonstrate the basic technological possibilities. The maximum deviation of local density of green C/SiC preform is less than 3 %, which is the worst-case estimation of the material uniformity over the area of final RB-SiC mirror blank. The issues related to lightweight structure and machining are analyzed. Based on a comparison of collected data on launched space mirrors and related developments, the manufactured mirror blanks can be assessed as meeting the basic requirements for small-aperture mirrors of Earth observation satellites and secondary mirrors of large-aperture telescopes.
engineering, manufacturing