Abstract:Abstract Fatigue behavior of woven melt infiltrated (MI) SiC/SiC ceramic matrix composites (CMCs) was investigated under a tension–tension fatigue condition in a combustion environment. A special experimental facility is designed to subject the CMCs under simultaneous mechanical and combustion conditions which is more representative of some conditions experienced by the hot section components of a jet engine. The MI SiC/SiC CMCs considered in this study consists of a SiC matrix densified with liquid Si infiltration, BN interphase, and reinforced with two different fibers, namely, Hi–Nicalon type S and Tyranno SA fibers. A high velocity oxygen fuel (HVOF) gun is used to create the representative combustion condition and a horizontal hydraulic MTS machine to apply the mechanical loading. Several fatigue tests were conducted at different stress levels with a stress ratio of 0.1, frequency of 1 Hz, and the specimen surface temperature at 1200 °C. Similar tests were conducted in an isothermal furnace condition at 1200 °C for comparison. Electrical resistance (ER) was used to monitor the tests. A reduction in the fatigue life was observed for the two MI systems under combustion conditions in comparison to the isothermal furnace condition at the same applied stress level. This is attributed to the presence of harsh combustion environment present in the burner rig. ER showed some promising results in monitoring the temperature and detecting damage in the specimen. Runout condition was set as 24 H (86400 cycles) in burner rig and 100 H (360000 cycles) in furnace environment. Specimens that achieved the runout condition were subsequently tested under monotonic tension testing at room temperature after cooldown to evaluate the residual properties. Residual strength results showed a significant strength reduction in both the furnace and burner rig environments. Post-test microscopy was conducted on the fracture surfaces of the failed specimens to understand the oxidation behavior and damage mechanisms.

Intermediate temperature degradation of a SiC/BN/SiC (MI) composite with holes at 500–900°C in steam

Tensile-tensile fatigue behavior of plain-woven SiCf/SiC ceramic matrix composites with differently spaced film cooling holes and environmental barrier coatings in high-temperature water-oxygen environments

Microstructural and mechanical evolution of SiCf/SiC composites in wet oxygen atmosphere above 1000 degrees C

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

Oxidation of SiC/BN/SiC ceramic matrix composites in dry and wet oxygen at intermediate temperatures

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Fatigue Characterization of SiC/SiC Ceramic Matrix Composites in Combustion Environment

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

Influence of an O2 Type Oxidizing Environment on SiCf/SiC Composites: Properties/Microstructure Relationship

Thermal stability of CVI and RMI SiC/SiC composites adopting Cansas 3303 SiC fibers

High-temperature tensile behavior of 3D SiC/SiC composites

Corrosion behavior of CVI 2D Cf/SiC composites under high temperature burner rig tests

Tensile Mechanical Behavior and Failure Mechanism of a Plain-Woven SiCf/SiC Composites at Room and Elevated Temperatures

Oxidation behavior of 3D SiCf/SiBCN composites at 800–1200 °C

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

High Temperature Fatigue Assessment of a SiCf/SiC Ceramic Matrix Composite Using Advanced Monitoring Techniques

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Design, fabrication, and testing of CVI-SiC/SiC turbine blisk under different load spectrums at elevated temperature

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Properties evolution and damage mechanism of SiC/SiC composites after thermal shock at 1300 °C

Failure Evaluation of a SiC/SiC Ceramic Matrix Composite During In-Situ Loading Using Micro X-ray Computed Tomography