Abstract:Silicon carbide fiber-reinforced silicon carbide ceramic matrix composites（SiCf/SiC） used in aero-engines are damaged or even failed due to the oxidation and corrosion by high-temperature and high-speed combustion gases. In this work，the gas generation device was used to simulate the complex gas environment in the aircraft engine，and the aviation kerosene mixed with liquid oxygen fuel in a certain proportion was ignited to form a high-temperature and high-speed combustion gas to assess the material. The oxidation test for 10 h and thermal shock test for 1000 cycles in combustion gas environment at 1200 ℃ were conducted on SiCf/SiC composites respectively. And the protective effect of environmental barrier coating（EBC）on SiCf/SiC composites was investigated. Uniaxial tensile tests were conducted on SiCf/SiC composites and SiCf/SiC-EBC composites after combustion gas environment assessment，and their fracture and cross-section micro-morphologies were observed by scanning electron microscopy. The results show that no significant oxidation of fibers and interphases is found in SiCf/SiC composites and SiCf/SiC-EBC composites after oxidation for 10 h in combustion gas environment，and their uniaxial tensile strength decreases by less than 2%. After 1000 thermal shock cycles in combustion gas environment，multiple micro-cracks are formed and oxidative corrosion of the interfacial layer occurs inside the SiCf/SiC composites，and the uniaxial tensile strength decreases by 41.3%. The EBC coating can effectively protect the SiCf/SiC composites from oxidation and corrosion of high-temperature gas，and the uniaxial tensile strength of SiCf/SiC-EBC composites decreases by 16.6% after 1000 thermal shock cycles.

Influence of an O2 Type Oxidizing Environment on SiCf/SiC Composites: Properties/Microstructure Relationship

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Influence of Oxidation Damages on Mechanical Properties of SiC/SiC Composite Using Domestic Hi-Nicalon Type SiC Fibers

Stress‐Oxidation Behavior of a Carbon/Silicon Carbide Composite in a High‐Temperature Combustion Environment

Oxidation Kinetics and Its Impact on the Strength of Carbon Short Fiber Reinforced C/SiC Ceramics

Mechanical Properties and Damage Analysis of SiCf/SiC and SiCf/SiC-EBC Composites in High-Temperature Combustion Gas Environment

Oxidation Behavior of SiC/SiC Composites in Air at High Temperature

High-Temperature Fatigue Degradation Behaviors of a 3D Braided C/SiC with a Thin Interlayer in Different Dry Oxygen Atmospheres

The Degradation Behavior of C/Sic Composites in Complex Environment

Erosion Behavior of C/SiC Composites in Atomic Oxygen

The Influence of Environmental Temperature on the Passive Oxidation Process in the C/SiC Composite

Non-Destruction Evaluation Method for Long-Term Oxidation Behavior of SiC/SiC Composites with Different Preforms in Wet Oxygen

Corrosion behavior of precracked SiCf/SiC composites under 1200–1300°C Na2SO4‐wet‐oxygen environment

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

SiC Performance of Coated Fuel Particles under High-Temperature Atmosphere of Air

Oxidation of SiC/BN/SiC ceramic matrix composites in dry and wet oxygen at intermediate temperatures

Mechanical properties and microstructure evolution of KD‐SA SiCf/BN/SiC CMCs oxidized at different temperatures

Oxidation behaviors of carbon fiber reinforced multilayer SiC-Si3N4 matrix composites

Oxidation resistance of SiCf/SiC composites with a PyC/SiC multilayer interface at 500 °C to 1100°C

Comparison of Oxidation Behaviors of 3D C/PyC/SiC and SiC/PyC/SiC Composites in an O2-Ar Atmosphere

Influence of the heat treatment on mechanical properties and oxidation resistance of SiC–Si3N4 composites