Boosting the collapse performance of Wax-binder-free silica based ceramic core via adding nano-alumina sol modified fused silica powder

Yi Qin,Xinsheng Sun,Yani Cheng,Lunkai Shi,Zixu Wang,Zhihao Qi,Yuan Fang,Jianfeng Zhu,Ting Zhao

DOI: https://doi.org/10.1007/s10971-024-06430-9

2024-06-21

Journal of Sol-Gel Science and Technology

Abstract:Wax-binder-free silica-based ceramic core with high collapsibility plays a critical role in precision casting. However, the collapse performance will dramatically reduce because the densification was induced by liquid phase sintering from the indispensable fused silica component, which makes the core hard to be removed by mechanical vibration, especially for the semi-enclosed parts. Herein, we propose a liquid phase sintering restraint strategy for improving collapsibility by adding surface-modified fused silica powder. The results show that a high-temperature resistant alumina/mullite shell can be formed by pre-coating alumina sol on the surface of fused silica powder after the processing of preheating and casting. Compared with utilizing pure fused silica powder, when adding 25 wt% modified fused silica substituted some part of pure fused silica, the flexural strength, porosity and bulk density of ceramic core reaches 5.95 MPa, 31.61% and 1.56 g/cm 3 respectively. These parameters completely satisfied the requirements of high collapsibility for casting, which is attributed to effectively inhibiting sintering and maintaining the porous structure by the alumina/mullite layer. Finally, the actual collapse experimental result shows that the cores can be completely removed through mechanical vibration lasting 30 min. This strategy offers a new method for improving the collapse properties of the wax-binder-free silica-based ceramic core by adding surface modified fused silica powder.

materials science, ceramics