Abstract:The ceramic core plays an important role in the preparation of aero-engine hollow blades, as it can directly determine the precision and pass rate of the cooling passage in the blade cavity. Sufficient high-temperature bending strength, high open porosity, and low sintering shrinkage are the main requirements for qualified ceramic cores. In order to prepare qualified ceramic cores with complex structures, in-situ mullite-reinforced Al2O3-based ceramic cores were successfully prepared using vat photopolymerization 3D printing technology. The in-situ synthesis of mullite was designed through thermodynamic analysis. The influence mechanisms of the sintering temperature and doping amount of fused silica on the open porosity, sintering shrinkage, and bending strength of the core were systematically investigated. With an increase in the sintering temperature and doping amount of fused silica, the porosity of the in situ mullite-reinforced ceramic core decreased. Sintering shrinkage increased with an increase in the sintering temperature and doping amount of fused silica. The cores containing 20 wt% fused silica showed the smallest sintering shrinkage. The bending strength increased with an increase in the sintering temperature and the doping amount of fused silica. A core doped with 20 wt% fused silica had the highest bending strength at 1773.15 K. Furthermore, 20 wt% fused silica doping, sintered at 1673.15 K, can be used to prepare in-situ mullite enhanced Al2O3-based cores with the best comprehensive properties. This core has a higher open porosity (40%), suitable bending strength of 25 MPa (at 1773.15 K), and lower sintering shrinkage in the Z direction. The significance of this study lies in the regulation of in-situ mullite generation and viscous flow in solid-liquid sintering by adjusting the doping amount of fused silica and the sintering process, and this opens up new pathways by the coordinated regulation of strength, open porosity, and sintering shrinkage of 3D printed ceramic cores.

Preparation of high-performance silica-based ceramic cores with B4C addition using selective laser sintering and SiO2–Al2O3 sol infiltration

Fabrication of high-performance silica-based ceramic cores through selective laser sintering combined with vacuum infiltration

Improved mechanical properties of SiB6 reinforced silica-based ceramic cores fabricated by 3D stereolithography printing

Effect of Al(OH) 3 on the Properties of Silica-based Ceramic Cores Prepared by Laser Powder Bed Fusion Combined with Vacuum Infiltration

Influence of Al2O3 content on mechanical properties of silica-based ceramic cores prepared by stereolithography

Microstructure and Crystallization Kinetics of Silica-Based Ceramic Cores with Enhanced High-Temperature Property

Infiltration of silica slurry into silica-based ceramic cores prepared by selective laser sintering based on pre-sintering

Enhanced 3D printed Al2O3 core via in-situ mullite

Influence of debinding parameter and nano-ZrO2 particles on the silica-based ceramic cores fabricated by stereolithography-based additive manufacturing

Reinforcement of silica-based ceramic cores based on amorphous and polycrystalline mullite fibers

Microstructure and properties evolution of silicon-based ceramic cores fabricated by 3D printing with stair-stepping effect control

Microstructure and mechanical properties of 3D-printed nano-silica reinforced alumina cores

Investigation on Properties of the Silica Ceramic Cores for the Hollow Blades Prepared by the Conversion of the Silicon Resin

Effect Of Silica Sol On The Properties Of Alumina-Based Duplex Ceramic Cores

High-performance 3D-printed Al2O3 cores for low-temperature sintering

Alumina-based ceramic mold with integral core and shell for hollow turbine blades fabricated by Laser powder bed fusion

Effects of ZrSiO4 content on properties of SiO2-based ceramics prepared by digital light processing

Experimental study on high temperature performances of silica-based ceramic core for single crystal turbine blades

Balancing flexural strength and porosity in DLP-3D printing Al<sub>2</sub>O<sub>3</sub> cores for hollow turbine blades

Additive manufacturing of low-shrinkage alumina cores for single-crystal nickel-based superalloy turbine blade casting

Fabrication of Silica-Based Ceramic Cores with Internal Lattice Structures by Stereolithography