Abstract:Silica-based ceramic cores play key roles in the casting of aeroengine blades, but they are highly limited by the poor high-temperature mechanical property. Here, fused mullite (FM) and sintered mullite (SM) powders were modified in silica-based ceramic cores, and the microstructure evolution and crystallization kinetics of ceramic cores depending on mullite types were studied. The ceramic cores with FM showed a dense microstructure and superior mechanical properties compared to those with SM. The ceramic cores with 10 wt.% of FM showed a crystallization activation energy of 1119.5 kJ/mol and a crystallization exponent of 1.74, and the values of 938.4 kJ/mol and 1.86 as SM were employed; the decreased crystallization activation energy and the elevated crystallization exponent by SM suggested that the excess impurities of alkali oxides and alkaline-earth oxides significantly promoted the crystallization of cristobalite. Even though the ceramic cores with mullite powders decreased slightly in the room-temperature mechanical property, their high-temperature flexure strength and creep deformation resistance were enhanced. The ceramic cores with 10 wt.% of FM showed excellent comprehensive performance, with linear shrinkage of 0.69%, room-temperature strength of 18.9 MPa, and high-temperature strength of 15.5 MPa, which satisfied the demands for hollow-blade casting.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is: to improve the mechanical properties of silica - based ceramic cores at high temperatures, especially the deformation resistance and high - temperature strength. Specifically, the authors focus on improving the microstructure and crystallization kinetics of silica - based ceramic cores by introducing different types of mullite (fused mullite and sintered mullite) powders, thereby enhancing their high - temperature performance. ### Background problems 1. **Poor high - temperature mechanical properties**: Although traditional silica - based ceramic cores have the advantages of low thermal expansion coefficient, chemical stability and good solubility, they are prone to softening and deformation at high temperatures, which affects their application in the casting of aero - engine blades. 2. **Influence of crystallization behavior**: Silica will crystallize into cristobalite at high temperatures. This phase change will lead to volume expansion and may introduce micro - cracks, thereby reducing the mechanical properties of the material. 3. **Lack of systematic research**: Although mullite, as a high - quality refractory material, has excellent thermal shock resistance and creep resistance, there are few studies on using it as a modifier for silica - based ceramic cores, and the relevant theoretical research is also relatively scarce. ### Solutions To improve these problems, the authors used two types of mullite powders (fused mullite and sintered mullite) as modifiers and studied their effects on the microstructure and crystallization kinetics of silica - based ceramic cores. Specific objectives include: - **Improve high - temperature strength**: By introducing mullite powders, enhance the deformation resistance of ceramic cores at high temperatures. - **Optimize crystallization behavior**: Study the effects of different types of mullite on the crystallization activation energy and crystallization index to control the amount and distribution of cristobalite generated. - **Reduce linear shrinkage rate**: By promoting the crystallization of cristobalite, increase the viscosity of ceramic cores and reduce the linear shrinkage rate during the sintering process. ### Results and discussion Through experiments and analysis, the authors found that: - Both fused mullite (FM) and sintered mullite (SM) can significantly improve the high - temperature performance of ceramic cores, especially the deformation resistance and high - temperature strength. - SM samples, due to containing more alkaline oxides and alkaline - earth metal oxides, promote the crystallization of cristobalite, showing lower crystallization activation energy and higher crystallization index. - The ceramic core containing 10 wt.% fused mullite (FM10) shows the best comprehensive performance, with a linear shrinkage rate of 0.69%, a room - temperature strength of 18.9 MPa, and a high - temperature strength of 15.5 MPa, meeting the requirements for hollow - blade casting. In conclusion, this study successfully improved the high - temperature performance of silica - based ceramic cores by introducing mullite powders, providing a new solution for the precision casting of aero - engine blades.

Microstructure and Crystallization Kinetics of Silica-Based Ceramic Cores with Enhanced High-Temperature Property

Reinforcement of silica-based ceramic cores based on amorphous and polycrystalline mullite fibers

Experimental study on high temperature performances of silica-based ceramic core for single crystal turbine blades

Microstructure and properties evolution of silicon-based ceramic cores fabricated by 3D printing with stair-stepping effect control

Effect of Al(OH) 3 on the Properties of Silica-based Ceramic Cores Prepared by Laser Powder Bed Fusion Combined with Vacuum Infiltration

Microstructure and mechanical properties of 3D-printed nano-silica reinforced alumina cores

Preparation of high-performance silica-based ceramic cores with B4C addition using selective laser sintering and SiO2–Al2O3 sol infiltration

Enhanced 3D printed Al2O3 core via in-situ mullite

Investigation on Properties of the Silica Ceramic Cores for the Hollow Blades Prepared by the Conversion of the Silicon Resin

Alumina-Based Ceramic Core Nano-Composites For Investment Casting

High-performance 3D-printed Al2O3 cores for low-temperature sintering

High-Temperature Mechanical Behaviors of SiO2-Based Ceramic Core for Directional Solidification of Turbine Blades

Influence of Al2O3 content on mechanical properties of silica-based ceramic cores prepared by stereolithography

Fabrication of high-performance silica-based ceramic cores through selective laser sintering combined with vacuum infiltration

Effect Of Silica Sol On The Properties Of Alumina-Based Duplex Ceramic Cores

Influence of debinding parameter and nano-ZrO2 particles on the silica-based ceramic cores fabricated by stereolithography-based additive manufacturing

Improved precision and mechanical properties of 3D‐printed silica ceramics via sintering temperature optimization

Microstructure Evolution and Mechanical Properties of Ceramic Shell Moulds for Investment Casting of Turbine Blades by Selective Laser Sintering

Anisotropy management on microstructure and mechanical property in 3D printing of silica-based ceramic cores

Particle size gradation design and performance enhancement of quartz cores for precision casting

Effect of Sintering Temperature on Microstructure and Mechanical Behavior of Alumina-Based Ceramic Shell by SLS