Abstract:The ceramic core plays an important role in the preparation of aero-engine hollow blades, as it can directly determine the precision and pass rate of the cooling passage in the blade cavity. Sufficient high-temperature bending strength, high open porosity, and low sintering shrinkage are the main requirements for qualified ceramic cores. In order to prepare qualified ceramic cores with complex structures, in-situ mullite-reinforced Al2O3-based ceramic cores were successfully prepared using vat photopolymerization 3D printing technology. The in-situ synthesis of mullite was designed through thermodynamic analysis. The influence mechanisms of the sintering temperature and doping amount of fused silica on the open porosity, sintering shrinkage, and bending strength of the core were systematically investigated. With an increase in the sintering temperature and doping amount of fused silica, the porosity of the in situ mullite-reinforced ceramic core decreased. Sintering shrinkage increased with an increase in the sintering temperature and doping amount of fused silica. The cores containing 20 wt% fused silica showed the smallest sintering shrinkage. The bending strength increased with an increase in the sintering temperature and the doping amount of fused silica. A core doped with 20 wt% fused silica had the highest bending strength at 1773.15 K. Furthermore, 20 wt% fused silica doping, sintered at 1673.15 K, can be used to prepare in-situ mullite enhanced Al2O3-based cores with the best comprehensive properties. This core has a higher open porosity (40%), suitable bending strength of 25 MPa (at 1773.15 K), and lower sintering shrinkage in the Z direction. The significance of this study lies in the regulation of in-situ mullite generation and viscous flow in solid-liquid sintering by adjusting the doping amount of fused silica and the sintering process, and this opens up new pathways by the coordinated regulation of strength, open porosity, and sintering shrinkage of 3D printed ceramic cores.

Performance of a Water-Soluble Ceramic Core and Its Application in Aluminum Casting

Water-Soluble Sand Core Made by Binder Jetting Printing with the Binder of Potassium Carbonate Solution

Alumina-Based Ceramic Core Nano-Composites For Investment Casting

Alumina-based ceramic cores prepared by vat photopolymerization and buried combustion method

Gelcasting of Alumina Based Ceramic Cores Containing Yttria for Single Crystal and Directional Solidification Blades

Effect Of Silica Sol On The Properties Of Alumina-Based Duplex Ceramic Cores

Comparative study on performance and microstructure of composite water-soluble salt core material for manufacturing hollow zinc alloy castings

Effect of Al(OH) 3 on the Properties of Silica-based Ceramic Cores Prepared by Laser Powder Bed Fusion Combined with Vacuum Infiltration

Enhanced 3D printed Al2O3 core via in-situ mullite

Preparation of high-performance silica-based ceramic cores with B4C addition using selective laser sintering and SiO2–Al2O3 sol infiltration

Basis for the Alkaline Removal Process Design of the Alumina-Based Ceramic Core

Influence of debinding parameter and nano-ZrO2 particles on the silica-based ceramic cores fabricated by stereolithography-based additive manufacturing

Improving High Temperature Properties of Alumina Based Ceramic Cores Containing Yttria by Vacuum Impregnating

High-performance 3D-printed Al2O3 cores for low-temperature sintering

Microstructure and properties evolution of silicon-based ceramic cores fabricated by 3D printing with stair-stepping effect control

Boosting the collapse performance of Wax-binder-free silica based ceramic core via adding nano-alumina sol modified fused silica powder

Fabrication of high-strength and anti-hydration water-soluble calcia-based ceramic core modified with nano-ZrO2 via direct ink writing method

3D printing of high-strength water-soluble salt cores via material extrusion

Leaching improvement of ceramic cores for hollow turbine blades based on additive manufacturing

Additive manufacturing of Al2O3 ceramic core with applicable microstructure and mechanical properties via digital light processing of high solid loading slurry

Microstructure and Crystallization Kinetics of Silica-Based Ceramic Cores with Enhanced High-Temperature Property