Alumina-based ceramic cores prepared by vat photopolymerization and buried combustion method

Dekun Kong,Anfu Guo,Yingbin Hu,Xiaoyan Zhou,Hailong Wu,Xunjin Li,Peng Qu,Shaoqing Wang,Shuai Guo

DOI: https://doi.org/10.1016/j.mtcomm.2023.107434

IF: 3.8

2023-11-10

Materials Today Communications

Abstract:Alumina (Al 2 O 3 )-based ceramic cores are extensively employed to form cavities within complex or difficult-to-form casting parts. As a conventional manufacturing process, investment casting requires molds and is labor-intensive. Therefore, it is crucial to develop a direct method for preparing Al 2 O 3 -based ceramic cores at a low cost. As an AM process, vat photopolymerization (VPP) can produce high-quality parts with smooth surface finish and fine details. Therefore, extensive attentions have been attracted to processing ceramic materials by VPP. Despite these benefits, the layer-by-layer accumulation strategy of VPP inevitably induces low bonding strength between adjacent layers, and induces cracks in the sintered parts. To mitigate these problems, burying VPP-printed Al 2 O 3 green bodies into silica has been proposed in this investigation. Results show that cracks and deformation problems have been reduced when the buried combustion method is adopted. To create Al 2 O 3 -based ceramic cores with desired porosity and flexural strength properties, process parameters have been optimized. A systematic study on how the inclusion of SiO 2 particles and variations in sintering temperature impact the microstructure and mechanical properties of Al 2 O 3 -based ceramic cores fabricated through VPP printing is presented. Based on experimental results, a 1300 °C sintering temperature is selected to produce appropriate shrinkages (4%∼8%), open porosity of over 20%, and flexural strength ranging from 20 to 50 MPa of ceramic cores.

materials science, multidisciplinary