Abstract:High-strength, high-porosity and relatively low-shrinkage ZrO 2 ceramics were successfully fabricated by material extrusion 3D printing technology via optimizing CaCO 3 addition and sintering temperature. The effects of different CaCO 3 additions on the performance, phase formation, and microstructure of porous ZrO 2 ceramics sintered at different temperatures were systematically investigated and discussed. The results showed that flexural strength, porosity and shrinkage of the ZrO 2 ceramics were significantly affected by CaCO 3 addition and sintering temperature. The appropriate addition of CaCO 3 could promote sintering and phase transformation of m-ZrO 2 , increase the number and size of pores in the matrix. The corresponding flexural strength and porosity of the sintered samples increased, while the shrinkage rate decreased. The raised sintering temperature appropriately facilitated the formation of CaZrO 3 . Microstructural analysis indicated that CaZrO 3 exhibited a larger polyhedral bulk morphology, mainly distributed at the edges of pores, which could stabilize the pore structure and thicken the sintering necks, and thereby exhibiting well-balanced comprehensive performance. The ZrO 2 ceramics with high flexural strength, high porosity and relatively low shrinkage rate were achieved by adding 15 wt% CaCO 3 and sintering at 1450 °C. The resulting flexural strength and porosity were 27.33 MPa and 67.62 %, respectively, presenting an improvement of 563.35 % and 13.69 % compared to ZrO 2 ceramics without CaCO 3 . Moreover, the shrinkage rates in the X-direction (9.98 %), Y-direction (9.62 %), and Z-direction (9.94 %) significantly reduced, decreasing by 38.28 %, 38.10 %, and 41.46 %, respectively.

Fabrication of high-strength and anti-hydration water-soluble calcia-based ceramic core modified with nano-ZrO2 via direct ink writing method

Influence of debinding parameter and nano-ZrO2 particles on the silica-based ceramic cores fabricated by stereolithography-based additive manufacturing

Direct ink writing additive manufacturing of porous alumina-based ceramic cores modified with nanosized MgO

Achieving high-strength, high-porosity and relatively low-shrinkage in extrusion-based 3D printed ZrO 2 ceramics by adjusting CaCO 3 addition and sintering temperature

Performance of a Water-Soluble Ceramic Core and Its Application in Aluminum Casting

Optimization of the injection molding process for development of high performance calcium oxide -based ceramic cores

Continuous carbon fiber reinforced ZrB2-SiC composites fabricated by direct ink writing combined with low-temperature hot-pressing

UV-Curing Assisted Direct Ink Writing of Dense, Crack-Free, and High-Performance Zirconia-Based Composites With Aligned Alumina Platelets

Fused silica ceramic core based on network-structured zircon design via 3D printing

Fabrication of Silica-Based Ceramic Cores with Internal Lattice Structures by Stereolithography

Compositional optimization of high-solid-loading ceramic cores via 3D printing

Fabrication of High-Performance Al2O3-ZrO2 Composite by a Novel Approach That Integrates Stereolithography-Based 3D Printing and Liquid Precursor Infiltration

Preparation and properties of high-porosity ZrB2-SiC ceramics by water-based freeze casting

Preparation of Y₂O₃ Coated CaO Ceramic Cores with Anti-Hydration Performance and High-Interface Stability Against Interface Reaction of Ti-6Al-4V Alloys

Rapid Fabrication of High-Performance CaO-Based Integral Ceramic Mould by Stereolithography and Non-Aqueous Gelcasting

A novel composite binder design for direct ink writing alumina-based ceramics with enhanced strength at low sintering temperature

A Strategy to Obtain a High-Density and High-Strength Zirconia Ceramic Via Ceramic Injection Molding by the Modification of Oleic Acid

Water-Soluble Sand Core Made by Binder Jetting Printing with the Binder of Potassium Carbonate Solution

Fabrication of Coloured Zirconia Ceramics by Infiltrating Water Debound Injection Moulded Green Body

Effect of Chopped ZrO2 Fiber Content on the Microstructure and Properties of CaO-Based Integral Ceramic Mold

Improved mechanical properties of SiB6 reinforced silica-based ceramic cores fabricated by 3D stereolithography printing