Enhancing fracture strength of ceramic core using sodium silicate as the binder

Hye‐Yeong Park,Seung Hwa Jung,Eun‐Hee Kim,SeungCheol Yang,Yeon‐Gil Jung

DOI: https://doi.org/10.1111/ijac.14070

2022-04-24

International Journal of Applied Ceramic Technology

Abstract:Ceramic cores used in the casting must exhibit high heat resistance because they come in direct contact with molten metals. Therefore, in this study, ceramic cores with high heat resistance and fracture strength were fabricated using sodium silicate as the binder instead of a commonly used organic binder. In addition, the prepared ceramic core was coated with Si and Si‐Na precursors as the inorganic binder to improve the firing strength of the ceramic core. The thermal stability and firing strength of the sample were investigated. The results revealed that the firing strength of the ceramic core was significantly improved up to 15.2 MPa owing to the formation of a glass phase between the ceramic particles, which was formed by the reaction of sodium silicate and the inorganic binder precursor. In addition, the core was completely decomposed in a NaOH solution at a relatively low temperature of 60°C, indicating the excellent elution properties of the sample. These results indicate that the method proposed in this study is suitable for the preparation of ceramic cores with high fracture strength and excellent elution behavior.This article is protected by copyright. All rights reserved

materials science, ceramics