Abstract:This work investigated the influence of tempering conditions coupled with cryogenic treatment on thermal stabilization of retained austenite and residual stress distributions in carbonitrided 18CrNiMo76 low alloy steel samples. The carbonitriding conditions were set to enable attaining surface carbon and nitrogen content of 0.87 and 0.34 mass.-percent respectively. After carbonitriding, some of the samples were subjected to varying tempering conditions followed by cryogenic treatment at -120 °C using nitrogen gas. Analysis of both retained austenite and residual stresses was conducted using X-ray diffraction. In the as-quenched state, carbonitrided samples contained 52 mass.-percent. Samples that were directly subjected to the cryogenic treatment after quenching retained only about 20 mass.-percent of austenite. Samples subjected to variant tempering conditions coupled with cryogenic treatment retained at least 30 masses.-percent of austenite. A thermal stabilization of retained austenite which increases with increasing temperature was identified. On tempering at 240°C for 14 hours retained austenite becomes unstable and decomposes to bainite leading to the low initial amount of retained austenite before cryogenic treatment. It can be concluded that the tempering process coupled with cryogenic treatment leads to an increasing hardness, to higher compressive residual stresses as well as to a shift of the location of maximum compressive residual stress toward the surface.

Effects of Retained Austenite upon Softening during Low-temperature Tempering in Martensitic Carbon Steels

Effect of N on the Precipitation Behaviours of the Reduced Activation Ferritic/martensitic Steel CLF-1 after Thermal Ageing

Influence of Tempering and Cryogenic Treatment on Retained Austenite and Residual Stresses in Carbonitrided 18CrNiMo7-6 Low Alloy Steel

Effect of Retained Austenite on Austenite Memory of a 13% Cr–5% Ni Martensitic Steel

Stability of retained austenite in high carbon steel – Effect of post-tempering heat treatment

Effect of Austenitizing Temperature and Retained Austenite on Mechanical Properties of 2200MPa Grade Ultra-High Strength Steels

Tempering Effects on the Stability of Retained Austenite and Mechanical Properties in a Medium Manganese Steel

The Role of Retained Austenite on the Mechanical Properties of a Low Carbon 3Mn-1.5Ni Steel

Effects of Ni content and tempering temperatures on microstructure and properties of medium-carbon cast steel

Microstructure Evolution and Mechanical Properties during Long-term Tempering of a Low Carbon Martensitic Stainless Bearing Steel

Enhancing Ductility of Martensitic Steels Through Cryogenic Treatment

Effect of Austempering Processes on the Tensile Properties and the Work-Hardening Behavior of Austempered Bainitic Steels Below the Martensite Start Temperature

Investigation of the Influence of Austempering Processing on Retained Austenite Amount of Austempered High Silicon Cast Steel

Thermal stability of retained austenite in bainitic steel: an in situ study

Effects of Austenitizing Conditions on the Microstructure of AISI M42 High-Speed Steel

Effect of Tempering Temperature and Carbide Free Bainite on the Mechanical Characteristics of a High Strength Low Alloy Steel

Influence of Austenitizing Temperature on the Microstructure and Mechanical Properties of an Fe-Cr-Ni-Mo-Ti Maraging Stainless Steel

Effect of Tempering on the Bainitic Microstructure Evolution Correlated with the Hardness in a Low-Alloy Medium-Carbon Steel

Effect of Austempering Treatment on Microstructure and Mechanical Properties of M50NiL Bearing Steel

Effect of Silicon, Chromium and Molybdenum on Resistance to Temper Softening of Medium-carbon Martensitic Steel

Kinetics of Martensite/Austenite Decomposition during Tempering of Ultrafine Nano-Bainitic Steels