Abstract:Cold-drawn pearlitic steel wires exhibit ultrahigh strength and have important applications where high strength and wear resistance are required. The hypereutectoid compositions present a promising potential for increasing the mechanical properties, especially the strength. The austenitization process strongly influences the following pearlitic microstructure and thus the mechanical properties. Continuous heating is always used in the industrial processing. However, the austenitization of pearlite in hypereutectoid steels during continuous heating has not been investigated systematically. In this work, the dilatometer and DSC were employed to investigate the austenitization kinetics of hypereutectoid steels during continuous heating. Microstructure evolution was observed with SEM and EBSD. The dilatometer and DSC curves were analyzed with derivative method. The whole austenitization can be divided into five stages: initial microstructure, reverse eutectoid transformation, retained cementite dissolution, homogenization and homogeneous austenite. Tangent method was used for measuring the critical temperatures of different stages. Experimental determination of transformed fraction was obtained through the lever method. Calculation with Thermo-Calc and Dictra software was carried out for the austenitization and considered to be a reasonable result by comparing with the experimental data. There is a turning point for the reduction rate of cementite and formation of austenite at the finishing temperature of reverse eutectoid transformation, which is similar with the austenitization in low carbon steel and spheroidal pearlite of hypereutectoid steel. Effects of heating rates, initial microstructure and carbon content were studied by varying the relevant parameters. Higher heating rate in- creases the starting and finishing temperatures of reverse eutectoid transformation and widens the temperature range, has no effect on the finishing temperature of retained cementite dissolution, increases the finishing temperature of homogenization. Coarser initial pearlitic microstructure increases the starting and finishing temperatures, widens the temperature range for reverse eutectoid transformation, increases the finishing temperature for retained cementite dissolution and homogenization. Enhancement of carbon content has little effect on the reverse eutectoid transformation, but increases the finishing temperature for retained cementite dissolution and homogenization. The effects mentioned above on the austenitization kinetics were discussed for mechanism analysis and compared with the observations of relevant systems provided by other research.

Investigation of the Influence of Austempering Processing on Retained Austenite Amount of Austempered High Silicon Cast Steel

Fracture Toughness of Austempered High Silicon Cast Steel

Morphology of Retained Austenite and Its Effects on the Mechanical Properties of High Silicon Cast Steel

Mechanisms of Strengthening and Toughening of Austempered High Silicon Cast Steel

Effects of Ti, V, and Rare Earth on the Mechanical Properties of Austempered High Silicon Cast Steel

Effects of Austempering Temperature on Strength, Ductility and Toughness of Low-C High-Al/Si Carbide-Free Bainitic Steel

Investigation on Heat Treatment Process of Austempered Ductile Iron

Microstructure and properties of an advanced high-strength steel after austempering treatment

Investigation on the Interrelationship between the Chemical Composition, Heat Treatment Parameters and the Phase Transformation Process, Microstructure Evolution and the Mechanical Properties of Austempered Steel

Effect of Austenitized Holding Temperature on Microstructure and Properties of Low-carbon Steel After I&Q&P Treatment

Tempering Effects on the Stability of Retained Austenite and Mechanical Properties in a Medium Manganese Steel

Microstructure and Mechanical Properties of Low- and Medium-Carbon Si-Rich Low-Alloy Steels Processed by Austemping after Intercritical Annealing

Effects of Retained Austenite upon Softening during Low-temperature Tempering in Martensitic Carbon Steels

Microstructure and Mechanical Properties of A New Type of Austempered Boron Alloyed High Silicon Cast Steel

Application of Rietveld Refinement to Investigate the High Chromium White Cast Iron Austempered at Different Temperatures

Effect of Austenitizing Temperature and Retained Austenite on Mechanical Properties of 2200MPa Grade Ultra-High Strength Steels

Investigation of Austenitization During Continuous Heating Process in Hypereutectoid Steels

Fracture toughness improvement of austempered high silicon steel by titanium, vanadium and rare earth elements modification

Effect of Prior Austenite Grain Size on Austenite Reversion, Bainite Transformation and Mechanical Properties of Fe-2Mn-0.2C Steel

Effect of austempering temperature on microstructure and cyclic deformation behaviour of multiphase low-carbon steel

Thermal Stability Of Retained Austenite In High-Carbon Steels During Cryogenic And Tempering Treatments