Abstract:Cold-drawn pearlitic steel wires have the highest strength of all steel products. It is a promising way to enhance the mechanical properties by increasing the carbon content. However, the proeutectoid cementite forms easily due to the hypereutectoid composition and deteriorates the mechanical and processing properties of steel wires. It is important for hypereutectoid steel wire drawing to achieve a fine and fully pearlitic microstructure without proeutectoid cementite. The austenitization and following continuous cooling process were simulated in the dilatometer for a hypereutectoid steel. The microstructure was observed with OM and SEM. The transformation temperature, prior-austenite grain size, pearlitic interlamellar spacing and proeutectoid cementite thickness were determined by dilatometric curves or OM/SEM images. The austenite grain size increases rapidly with a higher temperature and almost keeps invariant with a longer austenitization time. Faster cooling rate, higher austenitization temperature or longer austenitization time decrease the starting and finishing temperature of phase transformation, widen the temperature range, refine the pearlitic interlamellar spacing and suppress the proeutectoid cementite precipitation (reduce the thickness or make it discontinuous). However, it is easy to form martensite which is bad for the homogeneity of pearlitic microstructure by increasing the cooling rate or austenitization temperature simply. A fine pearlite in a pseudoeutectoid microstructure is achieved by extending the austenitization time to 60 min and controlling the austenitization temperature and cooling rate. Discontinuous proeutectoid cementite is observed in the samples with the higher austenitization temperature. Higher austenitization temperature and longer time are helpful to weaken the carbon concentration gradient. The homogeneous carbon distribution restrains carbon diffusion for cementite nucleation during the proeutectoid cementite precipitation and pearlite transformation, which decreases the transformation temperature. Compare to pearlite transformation, the proeutectoid cementite precipitation is affected more strongly by the carbon diffusion due to a longer diffusion distance. Therefore, the precipitation amount of proeutectoid cementite is reduced if the carbon diffusion is restrained. The amount of grain corner and grain edge reduce more dramatically than that of grain boundary if austenite grain size increases. The proeutectoid cementite only nucleates in grain corner and grain edge. The pearlite nucleation can form in grain boundary. Therefore, the larger austenite grains result in the sharp reduction in the sites for nucleation of proeutectoid cementite. Then, the amount of proeutectoid cementite are reduced and the morphology becomes discontinuous.

Investigation of Austenitization During Continuous Heating Process in Hypereutectoid Steels

Effects of austenitization and cooling rates on the microstructure in a hypereutectoid steel

EFFECTS OF AUSTENITIZATION AND COOLING RATESON THE MICROSTRUCTURE IN A HYPER-EUTECTOID STEEL

Kinetic Transitions and Mn Partitioning During Austenite Growth from a Mixture of Partitioned Cementite and Ferrite: Role of Heating Rate

Modeling of Austenite Decomposition during Continuous Cooling Process in Heat Treatment of Hypoeutectoid Steel with Cellular Automaton Method

Dilatometric and Microstructural Investigations on Austenite Decomposition under Continuous Cooling Conditions in a Cu-Bearing High-Strength Low-Alloy Steel

EBSD investigation for influences of austenitization time and cooling rate on microstructure in a ultrahigh carbon steel

Effect of Austenite Grain Size on Phase Transformation Structure of Low‐Carbon Microalloyed Steel

Investigation on the Interrelationship between the Chemical Composition, Heat Treatment Parameters and the Phase Transformation Process, Microstructure Evolution and the Mechanical Properties of Austempered Steel

Atom-probe tomographic and dilatometric studies of phase-transformations after inter-critical annealing of a low-carbon dual-phase steel

Origin of Austenitization-Dependent Eutectoid Transformation in High-Speed Steel: Revisiting the Role of Primary Carbide

Austenite Formation and Cementite Dissolution During Intercritical Annealing of a Medium-Manganese Steel from a Martensitic Condition

Effect of Rapid Heating and Quenching on Microstructure and Mechanical Properties of High Strength Low Alloy Steel

Effect of Austenitizing Temperature on Pearlite Transformation of a Medium-Carbon Steel

Insight into the induction hardening behavior of a new 0.40% C microalloyed steel: Effects of initial microstructure and thermal cycles

Development of Fully Pearlitic Microstructure in a Hypoeutectoid Steel

Effect of Austenite Grain Coarsening on Rheological Behavior of Low-carbon High-strength Steel at High Temperature

Effects of Different Austenitising Conditions on the Strength–Ductility Balance in a High-Strength Low-Alloy Steel

Cellular Automaton Modeling Of Austenite Nucleation And Growth In Hypoeutectoid Steel During Heating Process

Investigation of the Influence of Austempering Processing on Retained Austenite Amount of Austempered High Silicon Cast Steel

Prediction of the Non-Isothermal Austenitization Kinetics of Fe-C-Cr Low Alloy Steels with Lamellar Pearlite Microstructure