Influence of Austenitizing Temperature on the Microstructure and Mechanical Properties of an Fe-Cr-Ni-Mo-Ti Maraging Stainless Steel

Yong Lian,Minyu Ma,Jin Zhang,Jinfeng Huang,Wen Gao,Zunjun Zhang,Chao Zhao

DOI: https://doi.org/10.1007/s11665-019-04279-6

IF: 2.3

2019-08-19

Journal of Materials Engineering and Performance

Abstract:The influence of austenitizing temperature on the microstructure and mechanical properties of an Fe-Cr-Ni-Mo-Ti maraging stainless steel was investigated. The grain size, Laves phase, and retained austenite in steels given different solution treatments were observed using optical microscopy, scanning electron microscopy, and x-ray diffraction. Relationships with mechanical properties were measured by tensile testing. The grain growth rate was relatively slow at temperatures of 800-1000 °C then rapidly increased at higher temperatures. Low-temperature austenitization augmented the retention of austenite, the fraction of which decreased with an increase in austenitizing temperature. The Laves phases, which precipitated in austenite during austenitization at 800-900 °C, were preserved after quenching. The solution treatment had a significant effect on the final tensile properties of the steel after aging, due to the presence of retained austenite and Laves phase reducing its strength.

materials science, multidisciplinary