Age-Hardening Behaviour and the Factors of 00Cr12Ni9Mo4Cu2 Maraging Stainless Steel and Its Factors

Li Ju,Du Qiaolian,Wang Xiaoxiang

DOI: https://doi.org/10.3321/j.issn:1002-185x.2007.z3.063

2007-01-01

Rare Metal Materials and Engineering

Abstract:The effect of the solid solution temperature, cold working and aging on the microstructure and hardness of 0oCr12Ni9Mo4Cu2 maraging stainless steel was studied by means of optical microscopy, hardness testing, X-ray diffractometry (XRD). The results show that the alloy achieveed high increment of the hardness when solid solution treatment was conducted at 1050 similar to 1100 degrees C. The hardness increased almost linearly with the increase of cold working. The increment of the hardness achieved the highest value with 75% cold working, and 450 degrees C was the preferred temperature for age-hardening, at which the hardness HV reached 6550 MPa for 2 h and softening did not occurred within 24 h.