Abstract:Digital light processing (DLP) 3D-printed Si3N4 ceramics, known for their exceptional performance, offer distinct advantages in meeting the high-strength and complex structural demands of industries such as aerospace, semiconductors, healthcare, automotive, energy, and machinery. However, due to Si3N4's strong chemical stability, low diffusion rate, low self-sintering ability, and high melting point, achieving densification under conventional sintering conditions is challenging. As a result, sintering additives are essential to promote the sintering process, lower the sintering temperature, improve densification, and enhance performance. In this study, 45 vol% Si3N4 slurries were prepared using DLP 3D printing technology, incorporating nine different combinations of sintering additives, including aluminum oxide (Al2O3), yttrium oxide (Y2O3), and aluminum nitride (AlN), in various ratios with Si3N4. The slurries were then sintered at 1800 °C for 2 h under a 1 MPa N2 atmosphere. Additionally, the phase composition, microstructure, grain distribution, and crack propagation of the materials. The results showed that a Si3N4 to Al2O3 and Y2O3 ratio of 95:2.5:2.5 produced elongated β-Si3N4 grain structures and enhanced density, achieving a maximum Vickers hardness of 12.88 ± 0.52 GPa. Additionally, the synergistic toughening effect of the rod-like β-Si3N4 grains and sintering aids significantly improved the fracture toughness of the Si3N4 ceramic matrix, with a flexural strength of 540.63 ± 10.05 MPa and a fracture toughness of 4.92 ± 0.07 MPa·m1/2. This study lays the foundation for the future application of 3D-printed Si3N4 ceramics, optimization of sintering aid combinations at different ratios, and performance enhancement in extreme environments.

Realizing mechanical property improvement and coloration in Si3N4 ceramics by rare earth-doping

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Synergistic regulation of color and mechanical properties of silicon nitride ceramics via engineering hollow structures of Eu-enriched secondary phases

Colored Si3N4 ceramics via constructing Nd3+ doped core‐shell structures

Mechanical and electromagnetic shielding properties of colored Si3N4 ceramics

Effect of rare earths on mechanical properties and microstructures of Si3N4-based ceramics

Influences of Rare-Earth Oxide Additives on the Formation and Properties of Porous Si2N2O Ceramic

Rapid fabrication of Si3N4 ceramics with gradient appearance and microstructure

Effect of Rare Earth Additives on Properties of Silicon Nitride Ceramics

Oxidation behavior and mechanical property of Si3N4 ceramics with rare earth oxide addition

The Effects of the Single Additive on the Fabrication of Rod-like β-Si3N4

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Mechanical Property and Oxidation Behavior of Self-Reinforced Si3N4 Doped with Re2O3 (Re=Yb, Lu)

The effect of additives on sintering behavior and strength retention in silicon nitride with RE-disilicate

Effect Of Rare-Earth Additives On Thermal Conductivity, Mechanical And Electrical Properties Of Silicon Nitride Ceramics

Synergetic enhancement of electrical conductivity and infrared emissivity of SiC-MoSi2 ceramics via N doping

Thermal conductivity improvement in Si3N4 ceramics via grain purification

Impact of Sintering Aid Type and Content on the Mechanical Properties of Digital Light Processing 3D-Printed Si3N4 Ceramics

The effects of the single additive on the fabrication of rod-like beta-Si3N4

Preparation of the rod-like {beta}-Si{sub 3}N{sub 4} particles favoring the self-reinforcing Si{sub 3}N{sub 4} ceramics