Abstract:This paper introduces an approach to preparing high‐strength Si3N4 ceramics using vat photopolymerization with a bi‐phase particle size gradation strategy. The influence of different ratios of coarse β‐Si3N4 powders (Cβ) and fine α‐Si3N4 powders (Fα) on the slurry performance, microstructure evolution, and final ceramic strength was systematically studied. It was found that an appropriate particle size gradation can significantly reduce the viscosity of the slurry. The curing depth of Si3N4 slurries decreases with increasing Fα content, while the stability increases. During sintering, dissolved Fα‐Si3N4 not only directly precipitates into small elongated β‐Si3N4 grains but also onto the neighboring Cβ‐Si3N4, promoting the development of large elongated β‐Si3N4 grains and resulting in a bimodal microstructure distribution. The highest strength of Si3N4 ceramics was achieved with a ratio of 6:4 Cβ to Fα Si3N4 powders. Under these conditions, the Si3N4 ceramics exhibited a flexural strength of 472 MPa, significantly higher than that of Si3N4 ceramics prepared using pure Cβ/Fα powders. The strength improvement is primarily due to the well‐designed bi‐phase particle size gradation strategy, which optimizes slurry performance, minimizes defects that may be introduced during the green part printing process while controlling the microstructure evolution during sintering, achieves the ideal bimodal microstructure distribution. The outcomes of this research demonstrate the feasibility of using vat photopolymerization with bi‐phase particle size gradation for the preparation of high‐strength Si3N4 ceramics, which has great potential for application in the manufacturing of various ceramic products.

Rapid fabrication of Si3N4 ceramics with gradient appearance and microstructure

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Realizing mechanical property improvement and coloration in Si3N4 ceramics by rare earth-doping

Effect of sintering temperature on hardness gradient of Si3N4 ceramics fabricated by spark plasma sintering

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Colored Si3N4 ceramics via constructing Nd3+ doped core‐shell structures

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Effect of Initial Phase Composition on the Phase Composition, Microstructure, and Mechanical Properties of Si3N4 Ceramics

Microstructure and properties of porous Si3N4 ceramics by gelcasting-self-propagating high-temperature synthesis (SHS)

Microstructure and mechanical properties of spark plasma sintered SiC–B4C gradient ceramics with Al additive

Preparation of graded silicon nitride ceramics with high mechanical performance using β-Si 3 N 4 seeds

Microstructure, Mechanical and Dielectric Properties of Highly Porous Silicon Nitride Ceramics Produced by a New Water-Based Freeze Casting

Preparation of high‐strength Si3N4 ceramics via vat photopolymerization: A bi‐phase particle size gradation strategy

Fabrication of Si3N4 ceramics with improved thermal conductivity by carbothermal reduction and two‐step sintering

Synergistic Reinforcement of Si3N4 Based Ceramics Fabricated via Multiphase Strengthening under Low Temperature and Short Holding Time

Microstructure and Properties of Porous Si3n4 Ceramics with A Dense Surface

Cold spray and presureless sintering of zirconium phosphate bonded silicon nitride ceramics with porous gradient structure

Effects of sintering additives and sintering methods on the mechanical, antimicrobial and optical properties of Si3N4 bioceramics

Si3N4 Hollow Microsphere Toughened Porous Ceramics from Direct Coagulation Method Via Dispersant Reaction

Preparation of 3D printed silicon nitride bioceramics by microwave sintering