Microstructural Understanding of Flow Accelerated Corrosion of SA106B Carbon Steel in High-Temperature Water with Different Flow Velocities
Ying Hu,Long Xin,Chang Hong,Yongming Han,Yonghao Lu
DOI: https://doi.org/10.3390/ma16113981
IF: 3.4
2023-05-26
Materials
Abstract:All light or heavy water reactors fabricated with carbon steels suffer from flow-accelerated corrosion (FAC). The FAC degradation of SA106B with different flow velocities was investigated in terms of microstructure. As flow velocity increased, the major corrosion type changed from general corrosion to localized corrosion. Severe localized corrosion occurred in the pearlite zone, which can be the prior location for generating pits. After normalizing, the improvement in microstructure homogeneity reduced the oxidation kinetics and lowered cracking sensitivity, causing a decrease in FAC rates of 33.28%, 22.47%, 22.15%, and 17.53% at flow velocity of 0 m/s, 1.63 m/s, 2.99 m/s, and 4.34 m/s, respectively. Additionally, localized corrosion tendency was decreased by reducing the micro-galvanic effect and tensile stresses in oxide film. The maximum localized corrosion rate decreased by 21.7%, 13.5%, 13.8%, and 25.4% at flow velocity of 0 m/s, 1.63 m/s, 2.99 m/s, and 4.34 m/s, respectively.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering