Abstract:A high-temperature and high-pressure gas field in an oil field requires the use of super 13 chromium material due to corrosive environments. In the recent production process, there have been four consecutive cases of corrosion, fracture, and perforation of tubing nipples, which have brought enormous economic losses to the oilfield. This article analyzes the failure causes of these four tubing nipples and proposes preventive measures. In this paper, the macroscopic morphology, chemical composition, mechanical properties, metallography, and microscopic morphology of four failed tubing nipples have been analyzed. Combined with the field service conditions and string structure of the tubing nipples, it is believed that the failure of the tubing nipples is mainly due to the connection of carbon steel and stainless steel materials, forming a typical galvanic corrosion galvanic cell. The geometric and environmental factors of the materials exacerbate this corrosion. Eventually, severe galvanic corrosion occurred on the inner surface of the tubing nipple, resulting in severe wall thinning or partial perforation, and four tubing nipples failed. The failed tubing nipples in Wells A, B, and C have erosion marks, which are caused by the action of high pressure and high flow rate fluids in the well; The inner surface of the tubing nipple in Well D is rusty yellow, mainly due to the corrosion of its inner wall caused by the acid fracturing fluid injected earlier. At the same time, the string structure of four wells shows that the tubing nipple is located at the variable diameter node of the string. When the fluid in the well flows from the large hole into the smaller hole, the fluid in the well will change there, and its flow rate and pressure will also increase, further exacerbating the erosion in this area. With the development of deep wells containing carbon dioxide in oil fields and the application of carbon dioxide injection secondary oil recovery technology, the use of 13Cr martensitic stainless steel is also increasing. In order to avoid the occurrence of similar accidents that will bring huge economic losses to the oil field, it is recommended that the material of the pipe string (including accessories) of such wells be confirmed using a portable direct reading spectrometer before entering the well.

Experiment on the Anti-corrosion Property of Chrome Molybdenum Steel Tube in Naphthenic Acid Environment

Corrosion Behavior of 16mnr Steel and Welded Joints in High-Temperature Naphthenic Acid

The Effect of Ni201 Transition Layer on the Corrosion, Wear and Synergetic Cavitation Erosion-Corrosion Behavior of CMT-Monel K500 Coating

Study on High-Temperature Naphthenic Acid Corrosion of Type 304 and Type 316L Stainless Steel and Their Welded Joints

Summarization of High-temperature Naphthenic Acid Corrosion and Its Control Technique on Pipeline

Corrosion Performance Analysis of Tubing Materials with Different Cr Contents in the CO2 Flooding Injection–Production Environment

Experimental Investigation of Stress Corrosion Characteristics for 16mnr Steel in Nitrate Solution

A study on corrosion behavior of advanced weathering steel relying on Ni-Mo synergy under marine atmosphere

Experimental Assessment of Corrosion Properties for Materials Intended for Heavy Crude Processing

Effect of Mo on the Corrosion Resistance of Cr-Containing Steel in a Simulated Tropical Marine Atmospheric Environment

Effect of Presence of Chromium in the Composition of Low-Alloy Pipe Steels on the Corrosion Resistance in Oilfield Environments

Corrosion Study of Base Material and Welds of a Ni–Cr–Mo–W Alloy

Corrosion Analysis and Prevention of Tubing Nipples in Four Wells

Anti-corrosion Performance of Chromium-coated Steel in a Carbon Dioxide-saturated Simulated Oilfield Brine

Modelling and Analysis of the Corrosion Characteristics of Ferritic-Martensitic Steels in Supercritical Water

Study on the Corrosion Behavior of Aluminum Reinforced Austenitic Steel in Liquid Lead Bismuth at 550 °C

High-Cycle Microscopic Corrosion Fatigue Behavior and Life Prediction of 25 CrMo Steel Used in Railway Axle

Investigation of the Preparation, Corrosion Inhibition, and Wear Resistance of the Chromized Layer on the Surfaces of T9 and SPCC Steels

High-Cycle Microscopic Severe Corrosion Fatigue Behavior And Life Prediction Of 25crmo Steel Used In Railway Axles

Corrosion Behavior of FeCoNiCrAl High-Entropy Alloy in Molten NaNO3-KNO3

Influence of Cr Content on Hot Corrosion and a Special Tube Sealing Test of Single Crystal Nickel Base Superalloy