Abstract:Hot-dip galvanizing is the most economical way to improve the corrosion resistance of advanced high strength automobile steel. With the high trend of developing of automobile steel towards light-weight and high-strength, the contents of Si, Mn, Al alloy elements in steel increase accordingly. These alloy elements would be selectively oxidized during hot-dip galvanizing process, which affect in turn the wettability of steel surface and form different interface microstructures. However, its effect on the mechanical behavior of steel has never been known as clear as desired. Base on this point, the thermodynamics of the surface oxide and its effect on the interface microstructure of three high-strength automobile steels were studied after the same hot-dip galvanizing treatment as well as their tensile fracture behavior under different deformation conditions was in situ analyzed. Combined with the microstructure analysis and thermodynamic calculation, it can be concluded that different compositions of steel would produce different kinds of oxide on its surface. When Mn2SiO4 and SiO2 were formed as thermodynamic stable phases, it was difficult to form a continuous Fe2Al5Zn0.4 inhibition layer at the interface, zinc liquid could penetrate into the iron substrate and then form the brittle phase zeta-FeZn13, where the crack was easily to be obtained and expanded to the substrate, resulting in the decrease of mechanical properties. When MnO and Mn2SiO4 with a small amount were formed as thermodynamic stable phase, the Fe2Al5Zn0.4 inhibition layer can be obtained. Under the tensile stress, this crack generated at the interface and extended to the zinc layer. So, the fracture of the experimental steel was mainly resulted from the failure of substrate. When MnO and FeO were formed as metastable phase, Fe, as formed by aluminothermic reduction during hot-dip galvanizing, would reacted with zinc liquid to form Gamma-Fe11Zn40 phase in the zinc layer. The crack generated under the tensile stress and expanded in the zinc layer. Since the unreduced MnO layer at the interface exhibited a higher bonding strength with substrate, tensile fracture of the experimental steel was caused by the failure of substrate.

Analysis of the delayed cracking mechanism of an industrial hot-dip galvanized DP1180GI steel coil

A Review of Recent Developments in Coating Systems for Hot-Dip Galvanized Steel

Study on Bending Beam Delayed Cracking of Ultra High-strength DP Steel for Automotive Use

Effect of pre-strain on critical conditions for hydrogen-induced delayed cracking and crack nucleation characteristic of DP1180 steel

Effect of the Interface Microstructure of Hot-Dip Galvanizing High-Strength Automobile Steel on Its Tensile Fracture Behaviors

Study on Skin Pass Rolling Process Optimization and Performance of High Strength Hot-dip Galvanized Household Appliances Sheet

Uncovering the mechanism of the LME susceptibility for the galvanized and electrogalvanized DP 1180 steels

Hot-Dip Galvanizing of Carbon Steel after Cold Rolling with Oxide Scale and Hydrogen Descaling

Nanoscale surface analysis on second generation advanced high strength steel after hot dip galvanizing

Analysis of hydrogen-induced delayed cracking and hydrogen trapping behavior in plastically deformed quenching and partitioning steel

Deformation and damage mechanisms of zinc coatings on hot-dip galvanized steel sheets: Part II. Damage modes

Mechanical Properties of Hot-dip Galvanized Dual Phase Steel DP590 and Its Constitutive Model

Research of Microstructure and Mechanical Properties of the Cold Rolled Hot-Dip Galvanizing DP450 Steel with Low Carbon and High Chromium

Hot-dip galvanising behaviours of a CMnSiCr DP780 steel

Effect of Hot-Dip Galvanizing Process on Selective Oxidation and Galvanizability of Medium Manganese Steel for Automotive Application

Challenges in hot-dip galvanizing of high strength dual phase steel: Surface selective oxidation and mechanical property degradation

Changing Oxide Layer Structures with Respect to the Dew Point Prior to Hot-Dip Galvanizing of Δ-Trip Steel

Research of Microstructure and Properties of Resistance Spot Welded Joints of Galvanized DP Steel for Automobile

Analysis of hydrogen-induced cracking mechanism in quenching and partitioning steels

Effect of Dew Point on the Selective Oxidation and Reactive Wetting of DP980 Steel during Hot‐Dip Galvanizing

Study on zinc slag defects on surface of pure hot dip galvanized steel sheet