Effect of Surface Oxides on Bonding Properties of DP980
SHAO Rong,LIU Yong-zhuang,DONG Ni-ni,LI Run-chang,LIU Xin-hua,LIU Yang,LI Min,LI Xue-tao,CAO Jian-ping
DOI: https://doi.org/10.16490/j.cnki.issn.1001-3660.2023.03.035
2023-01-01
Surface Technology
Abstract:The purpose of this study was to investigate the effect of composition and content of surface oxides of high strength steel DP980 on bonding properties, so as to improve the bonding properties of dual-phase high strength steel. In this paper, 1wt.% acetic acid solution was used to etch the surface of high strength dual phase steels DP980 at different times. Scanning electron microscope（SEM） and transmission electron microscope（TEM） were used to observe the microstructures of oxides on the surface of high strength steel. Electro-Probe Microanalyzer（EPMA） were used to identify the elements distribution of DP980 before and after acid pickling. Glow discharge spectroscopy（GDS） were used to explore the variation of surface elements content with depth of DP980 treated with different pickling times. The XPS sputtering results further confirmed this conclusion. According to the peak fitting results of the high resolution X-ray photoelectron spectroscopy（XPS） spectra for Si and Mn elements, different kinds of surface oxides for high strength steel DP980 were characterized. In addition, the influence of pickling treatment on surface wettability of high strength steel was also analyzed by contact angle test. Finally, the bonding experiments of high strength steel treated with different pickling time were carried out to explore the influence of the content, morphologies and types of surface oxides on bonding properties of high strength steel surface.The results shows that Si, Mn and O elements are enriched on the surface of DP980, and the oxides on the surface of DP980 exists in the forms of Si Ox, Mn 2 SiO 4 , MnSiO 3 , MnO, etc. With the increasing of pickling time, the content of surface oxides on DP980 decreased, especially the SiOx content. Moreover, with the increasing of pickling time, the particle sizes of the surface oxides gradually decreased. In addition, the surface fluctuation in nanoscale of DP980 after pickling increased and the surface contact angle decreased. The bonding properties of DP980 after pickling are improved significantly. After 400 s pickling, the cohesion failure ratio of DP980 increased from 85% to 100%, the average shear strength increased from 0.54 MPa to 0.66 MPa, and the maximum shear force increased from 168.1 N to 206.4 N. This is due to the decrease of oxides particle size and content, which can effectively improve the surface wettability of the high strength steel. In addition, the removal of surface oxides can also enhance the interaction between the adhesive and DP980 matrix, thus improving the interface bonding strength.As a result, researchers could change the types and content of oxides on the surface of high strength dual phase steels by alloy composition design, continuous stripping process control, and some other methods, so as to improve the bonding performance of automobile steel plates.