Abstract:The hot -dip 55 wt%Al-Zn-1.6 wt%Si-(0-3)wt.%Mg alloy coatings were experimentally investigated, and the solidification behaviors and hot cracking susceptibility were simulated by means of CALPHAD (CALculation of PHAse Diagrams) method. The scanning electron microscopy (SEM), electron probe micro -analyzer (EPMA) and glow discharge spectrometer method (GDS) were utilized to determine the microstructures and the distribution of elements of the Al-Zn-Mg alloy coatings with different Mg contents. It is discovered that with the increase of Mg content, the percentage of the eutectic microstructure scales up, and the surface quality of the alloy coating is improved. Meanwhile, the bending properties of Al-Zn-Mg coatings with different Mg contents still requires further improvement according to the present bending test. Subsequently, the equilibrium solidification processes of the coatings were calculated using thermodynamic approach. In general, the calculated results reflect the solidified phases and the precipitated temperatures according to theory of equilibrium solidification. However, there still exist discrepancies between the thermodynamic calculation results and the observed experimental results during the practical galvanizing process, because the cooling rates were not taken fully into consideration. Consequently, the kinetic analysis was carried out to obtain the secondary dendrite arm spacing under different cooling rates. The cracking susceptibility index (CSI) was also calculated to predict the hot workability of the Al-Zn-Mg alloy coating. In summary, the appropriate increase of the cooling rate turns out be the effective approach to benefit the microstructure and the corrosion resistance of the Al-Zn-Mg coatings in the practical galvanizing process, and the coating is not suitable for the hot stamping process.

Hot-dip galvanising behaviours of a CMnSiCr DP780 steel

Effect of Hot-Dip Galvanizing Process on Selective Oxidation and Galvanizability of Medium Manganese Steel for Automotive Application

Hot-Dip Galvanizing of Carbon Steel after Cold Rolling with Oxide Scale and Hydrogen Descaling

Effect of Dew Point on the Selective Oxidation and Reactive Wetting of DP980 Steel during Hot‐Dip Galvanizing

Influence of Minor Alloying Elements on Selective Oxidation and Reactive Wetting of CMnSi TRIP Steel during Hot Dip Galvanizing

Nanoscale surface analysis on second generation advanced high strength steel after hot dip galvanizing

Effect of dew point during heating on selective oxidation behavior of C-Mn-Si-Al high strength steel

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Analysis of the delayed cracking mechanism of an industrial hot-dip galvanized DP1180GI steel coil

Effects of Alloying Elements on Surface Oxides of Hot-Dip Galvanized Press Hardened Steel

A Review of Recent Developments in Coating Systems for Hot-Dip Galvanized Steel

Effects of heating atmosphere on selective oxidation of a C-Mn-Si-Al high strength steel

Influence of Fe Oxidation on Selective Oxidation Behavior of Si and Mn Added in High Strength Sheet Steel

Investigation of Selective Oxidation and Reaction Wetting of Q&P Steel Under Different Dew Point During Continuous Galvanizing

Corrosion Properties of Steel Sheet with Zinc-Base Alloy Coatings

Effect of Sn Addition, Process Atmosphere pO2, and Annealing Time on the Selective Oxidation of a C-2Mn-1.7Si (Wt Pct) Advanced High-Strength Steel During Continuous Galvanizing

Effect of annealing process on surface selective oxidation behavior of C-Mn-Si high strength steels

The inhibition of MnO on Fe 2 Al 5 Zn x growth and associated three-dimensional nested phase distribution in the galvanized coating of high-Al low-Si dual phase steel

In-Situ Wettability Analysis of Al Coating Influence on Hot-Dip Galvanizing Properties of Advanced High-Strength Steels

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel