Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Guangrui Jiang,Haiquan Wang,Min Li,Guanghui Liu,Chunqian Xie

DOI: https://doi.org/10.1007/978-3-030-05861-6_93

2017-01-01

Abstract:Three hot-dip galvanizing coatings i.e.pure Zn,Zn-5％Al and Zn-2％Al-2％Mg were prepared respectively on sheets of a commercial interstitial free (IF) steel by a hot-dip process simulator (HDPS).Corrosion behavior of the coated steel sheets was studied by means of immersion test,electrochemical measurement and scanning electron microscope (SEM).Results show that the Zn-Al-Mg coating has the largest corrosion current density at the eady stage of immersion.While with the increasing immersion time,the corrosion current density of the Zn-Al-Mg decreases but those of the pure Zn and Zn-5％Al coatings increase.For the Zn-5％Al coating,diffusion characteristics could be found for its Nyquist curve,which means higher corrosion rate.However,for the Zn-Al-Mg coating,limited diffusion characteristics could be found for its Nyquist curve,which means a perfect coverage of corrosion products on the coating surface,in other word,the corrosion resistance was enhanced.