Abstract:The hot -dip 55 wt%Al-Zn-1.6 wt%Si-(0-3)wt.%Mg alloy coatings were experimentally investigated, and the solidification behaviors and hot cracking susceptibility were simulated by means of CALPHAD (CALculation of PHAse Diagrams) method. The scanning electron microscopy (SEM), electron probe micro -analyzer (EPMA) and glow discharge spectrometer method (GDS) were utilized to determine the microstructures and the distribution of elements of the Al-Zn-Mg alloy coatings with different Mg contents. It is discovered that with the increase of Mg content, the percentage of the eutectic microstructure scales up, and the surface quality of the alloy coating is improved. Meanwhile, the bending properties of Al-Zn-Mg coatings with different Mg contents still requires further improvement according to the present bending test. Subsequently, the equilibrium solidification processes of the coatings were calculated using thermodynamic approach. In general, the calculated results reflect the solidified phases and the precipitated temperatures according to theory of equilibrium solidification. However, there still exist discrepancies between the thermodynamic calculation results and the observed experimental results during the practical galvanizing process, because the cooling rates were not taken fully into consideration. Consequently, the kinetic analysis was carried out to obtain the secondary dendrite arm spacing under different cooling rates. The cracking susceptibility index (CSI) was also calculated to predict the hot workability of the Al-Zn-Mg alloy coating. In summary, the appropriate increase of the cooling rate turns out be the effective approach to benefit the microstructure and the corrosion resistance of the Al-Zn-Mg coatings in the practical galvanizing process, and the coating is not suitable for the hot stamping process.

Effects of Al contents on microstructure and properties of hot-dip Zn-Al alloy coatings on hydrogen reduced hot-rolled steel without acid pickling

Effects of Al content on microstructure and corrosion behavior of Zn-Al alloy coatings

Solidification microstructure of Zn-(0-6.0%)Al-4%Sb alloys used for hot-dip galvanizing

Effect of Al Content on the Long-Term Corrosion Behavior of Arc-Sprayed ZnAl Alloy Coatings

In-Situ Wettability Analysis of Al Coating Influence on Hot-Dip Galvanizing Properties of Advanced High-Strength Steels

Effect of Mg on the Corrosion Resistance of Hot-Dip Zn-Cu-Ti Alloy

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Study on the interface reaction layer of hydrogen reduction hot-rolled high-strength steel hot-dip galvanizing

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating

Effect of Dipping Time on Microstructure and Properties of Zn-1Al-2Mg Coating by Hot-Dipping Galvanizing

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide

Effect of Al Content on the Microstructure and Properties of Zn-Al Solder Alloys

Influence of Al contents on the long-term corrosion behaviors of cold-sprayed Zn-xAl coatings

Effects of Al-Mg on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

The Effects of B on the Microstructure and Corrosion Resistance of Zn–6Al–3Mg Alloy Coating

Effect of Al/Mg Ratio on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

Preparation, Wear Resistance, and Corrosion Performance of Arc-Sprayed Zn, Al, and Zn-Al Coatings on Carbon Steel Substrates

Experimental Measurements and Kinetic Investigation of Fe-Al Alloy Layer During the Galvanizing Process

Corrosion Properties of Steel Sheet with Zinc-Base Alloy Coatings

In-situ Zn-Al Layered Double Hydroxide Conversion Coatings Prepared on Galvanized Steels by a Two-Step Electrochemical Method