Abstract:The formation of a uniform Fe-Al inhibition layer with a proper thickness at steel interface during continuous hot-dip galvanizing process is a crucial issue for industrial production. The inhibition layer prohibits the nucleation and growth of brittle Fe-Zn intermetallic compounds which deteriorate the adhesion of the galvanizing coating and result in an inhomogeneous distribution of the coating. The inhibition layer was identified to be Fe2Al5 with some Zn dissolved in it. But Fe2Al5 inhibition layer was damaged with galvanized time increasing, will lose the inhibition to the Fe- Zn reaction. Nevertheless, there is no systematic and comprehensive investigation the causes of the inhibition layer is damaged. The aim of this work is to clarify the destabilization mechanism of Fe2Al5 inhibition layer. In the present study, the mass fraction of 0.2%Al was added into the zinc bath at 450 degrees C for hot dip galvanizing. SEM was used to observe the structure characteristics of the hot-dip galvanized coating. EDS was used to quantitatively analyze the micro area components of phases and also Used its line scan and mapping scan to qualitatively analyze the element change of the coating cross section. By means of the Miedema model and the Toop model, the thermodynamic values of the binary Fe-Al, Fe-Zn and ternary Fe2Al5Znx (eta) intermetallic compounds (IMC) in the coatings were calculated. The fundamental reason for the Fe-Zn reaction caused by Fe2Al5 destabilization with galvanized time increasing was analyzed. The results show that because Fe-Al IMC which is generate preferentially had more stable thermodynamic property than Fe-Zn IMC, the continuous Fe2Al5 intermetallic compound inhibition layer was produced preferentially at steel and zinc bath interface which inhibit the Fe-Zn reaction. However, with the galvanized time increasing, Fe2Al5 destabilization which led to the loss of inhibitory effect of Fe-Zn reaction and produced FeZn10 (delta). There are two kinds of destabilization mechanism of Fe2Al5 inhibition layer, one is that the local depletion of Al at Fe2Al5 and zinc bath interface result in erosion of Fe2Al5 by Zn and the formed Fe2Al5Znx caused the decrease of the systematic thermodynamic stability which led to erosion and decomposition of Fe2Al5 by Zn. At the same time, FeZn10 (delta) phase was produced between the Fe2Al5 and zinc bath interface. The phase transformation process can be described as: Fe2Al5 ->eta -> L+eta+delta -> L+delta. The other kind of destabilization mechanism is Zn diffused to the steel substrate by Fe2Al5 grain boundaries and directly produced 5 phase between Fe2Al5 and steel substrate interface, which caused outburst of Fe2Al5. The two kinds of Fe2Al5 destabilization mechanism are mutual coexistence and mutual competition, in particular conditions may be a mechanism to occupy absolute advantage.

Experimental Measurements and Kinetic Investigation of Fe-Al Alloy Layer During the Galvanizing Process

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating

Destabilization Mechanism of Fe-Al Inhibition Layer in Zn-0.2%Al Hot-Dip Galvanizing Coating and Related Thermodynamic Evaluation

Effects of Aluminum Concentration on the Formation of Inhibition Layer During Hot-Dip Galvanizing

Mesoscale Investigation of Reaction–diffusion and Structure Evolution During Fe–Al Inhibition Layer Formation in Hot-Dip Galvanizing

Characterization of hot-dip galvanized coating on dual phase steels

Study on Hot Dip and Coating Structure of 55% Al-Zn Alloy Coated Steel

Effect of Strip Entry Temperature on the Formation of Interfacial Layer During Hot-Dip Galvanizing of Press-Hardened Steel

Effects of Al contents on microstructure and properties of hot-dip Zn-Al alloy coatings on hydrogen reduced hot-rolled steel without acid pickling

The inhibition of MnO on Fe 2 Al 5 Zn x growth and associated three-dimensional nested phase distribution in the galvanized coating of high-Al low-Si dual phase steel

Study on the interface reaction layer of hydrogen reduction hot-rolled high-strength steel hot-dip galvanizing

Effect of Dew Point on Galvanizability in 4 Mass% Al Added Low Density Steel

Understanding the Formation Mechanism of Al-Rich Interfacial Layer during Galvanizing of Cu Pre-coated High-Strength Steel Sheet

Effect of Al Content on the Microstructure of Hot-Depped Zinc Coating on Hot Stamping Steel

In-Situ Wettability Analysis of Al Coating Influence on Hot-Dip Galvanizing Properties of Advanced High-Strength Steels

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

Effects of Heat Treatments on Phase Structure of Electrodeposition Aluminum Coatings on Different Substrates

Growth Process and Mechanism of Hot-Dip Galvanised Zn–5Al Coating on Steel

Microstructure Characteristics of Fe-Al Intermetallic Compound Coating Synthesized by Light Beam Alloying

Effects of Alloying Elements on Surface Oxides of Hot-Dip Galvanized Press Hardened Steel

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide