Abstract:The formation of a uniform Fe-Al inhibition layer with a proper thickness at steel interface during continuous hot-dip galvanizing process is a crucial issue for industrial production. The inhibition layer prohibits the nucleation and growth of brittle Fe-Zn intermetallic compounds which deteriorate the adhesion of the galvanizing coating and result in an inhomogeneous distribution of the coating. The inhibition layer was identified to be Fe2Al5 with some Zn dissolved in it. But Fe2Al5 inhibition layer was damaged with galvanized time increasing, will lose the inhibition to the Fe- Zn reaction. Nevertheless, there is no systematic and comprehensive investigation the causes of the inhibition layer is damaged. The aim of this work is to clarify the destabilization mechanism of Fe2Al5 inhibition layer. In the present study, the mass fraction of 0.2%Al was added into the zinc bath at 450 degrees C for hot dip galvanizing. SEM was used to observe the structure characteristics of the hot-dip galvanized coating. EDS was used to quantitatively analyze the micro area components of phases and also Used its line scan and mapping scan to qualitatively analyze the element change of the coating cross section. By means of the Miedema model and the Toop model, the thermodynamic values of the binary Fe-Al, Fe-Zn and ternary Fe2Al5Znx (eta) intermetallic compounds (IMC) in the coatings were calculated. The fundamental reason for the Fe-Zn reaction caused by Fe2Al5 destabilization with galvanized time increasing was analyzed. The results show that because Fe-Al IMC which is generate preferentially had more stable thermodynamic property than Fe-Zn IMC, the continuous Fe2Al5 intermetallic compound inhibition layer was produced preferentially at steel and zinc bath interface which inhibit the Fe-Zn reaction. However, with the galvanized time increasing, Fe2Al5 destabilization which led to the loss of inhibitory effect of Fe-Zn reaction and produced FeZn10 (delta). There are two kinds of destabilization mechanism of Fe2Al5 inhibition layer, one is that the local depletion of Al at Fe2Al5 and zinc bath interface result in erosion of Fe2Al5 by Zn and the formed Fe2Al5Znx caused the decrease of the systematic thermodynamic stability which led to erosion and decomposition of Fe2Al5 by Zn. At the same time, FeZn10 (delta) phase was produced between the Fe2Al5 and zinc bath interface. The phase transformation process can be described as: Fe2Al5 ->eta -> L+eta+delta -> L+delta. The other kind of destabilization mechanism is Zn diffused to the steel substrate by Fe2Al5 grain boundaries and directly produced 5 phase between Fe2Al5 and steel substrate interface, which caused outburst of Fe2Al5. The two kinds of Fe2Al5 destabilization mechanism are mutual coexistence and mutual competition, in particular conditions may be a mechanism to occupy absolute advantage.

Interface reaction of high-strength low-alloy steel with Al–43.4Zn–1.6Si (wt.%) metallic coating

Understanding the Formation Mechanism of Al-Rich Interfacial Layer during Galvanizing of Cu Pre-coated High-Strength Steel Sheet

Interfacial Bonding Mechanism in Al/coated Steel Dissimilar Refillfriction Stir Spot Welds

Effect of high entropy alloy as the interlayer on the interfacial microstructure and mechanical property of Al/steel bimetal by compound casting

Research on Hot-dipped Zn-6％Al-3％Mg Alloy Coatings Intermetallics Layer Growth

Effect of Zn Concentration on the Microstructure and Mechanical Properties of Al-Mg-Si-Zn Alloys Processed by Gravity Die Casting

The inhibition of MnO on Fe 2 Al 5 Zn x growth and associated three-dimensional nested phase distribution in the galvanized coating of high-Al low-Si dual phase steel

Study on the interface reaction layer of hydrogen reduction hot-rolled high-strength steel hot-dip galvanizing

Preparation and Analysis of Al-Mg Intermetallic Coating

Destabilization Mechanism of Fe-Al Inhibition Layer in Zn-0.2%Al Hot-Dip Galvanizing Coating and Related Thermodynamic Evaluation

Steel/refractory/slag interfacial reaction and its effect on inclusions in high-Mn high-Al steel

Effect of Strip Entry Temperature on the Formation of Interfacial Layer During Hot-Dip Galvanizing of Press-Hardened Steel

Effect of Flash-Ni Plating Layer on Interfacial Behavior of Zn-Al-Mg Coating/Dh780 Steel

Effects of Zinc Coating on Interfacial Microstructures and Mechanical Properties of Aluminum/steel Bimetallic Composites

Microstructure Characteristics of Fe-Al Intermetallic Compound Coating Synthesized by Light Beam Alloying

Effects of Al-Mg on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

Effect of Si content on interfacial reaction and properties between solid steel and liquid aluminum

Effects of Hot-Dip Galvanizing and Aluminizing on Interfacial Microstructures and Mechanical Properties of Aluminum/iron Bimetallic Composites

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

Interfacial Microstructure and Mechanical Properties of Al/steel Joints Fabricated Via Thermo-Compensated Resistance Brazing Welding with Cold Spray Zn Interlayer

Effects of Zn Interlayer on Microstructures and Mechanical Properties of TC4/AZ91D Bimetal via Solid–Liquid Compound Casting Process