Reaction Between Hot-Dip Aluminized Coating on Fe–Cr–B Cast Steel and Molten ZnCl2 Salt

Xianman Zhang,Qi Hu,Zhenhai Zheng

DOI: https://doi.org/10.1007/s12666-024-03342-8

2024-05-26

Transactions of the Indian Institute of Metals

Abstract:The reaction between MoAlB MAB phase and molten ZnCl 2 salt resulted in the formation of metastable Mo 2 AlB 2 MAB phase. In our previous work, it was first discovered by us that the periodic layered structure (PLS) was formed at the solid (Cr, Fe) 2 B/molten Al interface during hot-dip aluminizing and subsequent thermal diffusion treatment of Fe–Cr–B cast steel. The interaction between PLS form in situ, especially the Cr–Al–B MAB phase contained in the PLS, and molten ZnCl 2 salt was studied for the first time in this work. There were complex reactions between the PLS and molten ZnCl 2 . Specially, the Zn 2+ in the molten ZnCl 2 salt could partially occupy the positions of Al atoms in the Cr–Al–B MAB phase contained in the PLS through the A-site replacement reaction. The topochemical reaction was: Cr 3 AlB 4 (s) + ZnCl 2 (l) → Cr 3 (Al, Zn)B 4 (s) + Zn(l) + AlCl 3 (g).

metallurgy & metallurgical engineering