Abstract:The corrosion of steel structures in aggressive marine environments is a vital issue that induces significant degradation of their performance and lifespan. Herein, three arc-sprayed ZnAl coatings with varied Al contents of 0 wt.%, 15 wt.%, and 50 wt.% were deposited onto a hull steel substrate. The effect of Al content on the long-term corrosion protection performance of ZnAl coatings left in a chloride-containing solution for 840 h was systematically investigated. The evolutions of open-circuit potential, polarization curves, and electrochemical impedance spectroscopy of different ZnAl coatings during the long-term immersion test were examined. The morphologies and phase constitutions of the corrosion products were characterized. The results indicated that the corrosion rate of ZnAl coatings decreased as the Al content increased, and the ZnAl50 coating exhibited the most superior long-term corrosion protection performance. Moreover, for the three ZnAl coatings with an Al contents varying from 0 to 50%, their corrosion rate increased with immersion time in the initial 360 h due to the formation of the unstable and porous corrosion product ZnO; after 360 h immersion, their corrosion rate decreased with the prolonging of immersion time. This was revealed to be related to the formation of different corrosion products. ZnO and stable Al2O3 were the main corrosion products for the pure Zn coating and ZnAl15 coating, respectively. Al2O3 and powerful layered double hydroxide Zn6Al2(OH)16CO3·4H2O were found to be the dominant corrosion products of the ZnAl50 coating, which was responsible for its remarkable long-term corrosion protection performance.

Study on the structure and corrosion behavior of hot-dipped Zn–6Al–3Mg alloy coating in chlorine-containing environment

The initial corrosion mechanism of hot-dipping Zn–Al–Mg alloy coating in chloride-containing solution

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel

Effect of Al Content on the Long-Term Corrosion Behavior of Arc-Sprayed ZnAl Alloy Coatings

Formation and Evolution of Corrosion Products on Eutectic Microstructures: A Novel Study to Understand Corrosion Protection of Zn–Al–Mg Coatings

Effect of Mg on the Corrosion Resistance of Hot-Dip Zn-Cu-Ti Alloy

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Investigation of Zn alloy coating with submicron phases on magnesium alloy by the novel hot-dip process

Influence of Al contents on the long-term corrosion behaviors of cold-sprayed Zn-xAl coatings

Effects of Al-Mg on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

Effect of Dipping Time on Microstructure and Properties of Zn-1Al-2Mg Coating by Hot-Dipping Galvanizing

Study on corrosion mechanism of Al-Zn coatings in the simulated polluted marine atmosphere

Effects and mechanism of Zn on the structure and corrosion resistance of microarc oxidation coatings on aluminum alloy

Microstructure, Mechanical Properties and Corrosion Behaviors of Al–Li–Cu–Mg–Ag–Zn Alloys

Corrosion behavior and mechanism of electric arc-sprayed Al-Mg coating and Zn-Al-Mg pseudo-alloy coatings

Influencial mechanisms of elements and alloy phases on corrosion resistance of Zn-Al-Mg coated steel in atmospheric environments: A review

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide

Multi-scale study on the electrochemical behavior and corrosion mechanism of 5083 aluminum alloy with different microstructures in a NaCl environment

Microstructure and Corrosion Resistance of Zn-Al Diffusion Layer on 45 Steel Aided by Mechanical Energy

Balanced Anti-Corrosion Action of Reduced Graphene Oxide in Zn-Al Coating during Medium-Term Exposure to NaCl Solution

Influence mechanism of different elements and alloy phases on the corrosion resistance of Zn-Al-Mg coated steel in the atmospheric environment: A review