Abstract:The corrosion of steel structures in aggressive marine environments is a vital issue that induces significant degradation of their performance and lifespan. Herein, three arc-sprayed ZnAl coatings with varied Al contents of 0 wt.%, 15 wt.%, and 50 wt.% were deposited onto a hull steel substrate. The effect of Al content on the long-term corrosion protection performance of ZnAl coatings left in a chloride-containing solution for 840 h was systematically investigated. The evolutions of open-circuit potential, polarization curves, and electrochemical impedance spectroscopy of different ZnAl coatings during the long-term immersion test were examined. The morphologies and phase constitutions of the corrosion products were characterized. The results indicated that the corrosion rate of ZnAl coatings decreased as the Al content increased, and the ZnAl50 coating exhibited the most superior long-term corrosion protection performance. Moreover, for the three ZnAl coatings with an Al contents varying from 0 to 50%, their corrosion rate increased with immersion time in the initial 360 h due to the formation of the unstable and porous corrosion product ZnO; after 360 h immersion, their corrosion rate decreased with the prolonging of immersion time. This was revealed to be related to the formation of different corrosion products. ZnO and stable Al2O3 were the main corrosion products for the pure Zn coating and ZnAl15 coating, respectively. Al2O3 and powerful layered double hydroxide Zn6Al2(OH)16CO3·4H2O were found to be the dominant corrosion products of the ZnAl50 coating, which was responsible for its remarkable long-term corrosion protection performance.

Corrosion mechanisms of Al‐alloyed hot‐dipped zinc coatings in wet supercritical carbon dioxide

Corrosion Properties of Steel Sheet with Zinc-base Alloyed Coatings

Atmospheric corrosion of Zn–Al coatings in a simulated automotive environment

Corrosion Properties of Steel Sheet with Zinc-Base Alloy Coatings

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel

Effect of Al Content on the Long-Term Corrosion Behavior of Arc-Sprayed ZnAl Alloy Coatings

The characteristics of Zn–5Al–2Mg coating on low carbon steel by two-step galvanizing method

Effects of Al contents on microstructure and properties of hot-dip Zn-Al alloy coatings on hydrogen reduced hot-rolled steel without acid pickling

The initial corrosion mechanism of hot-dipping Zn–Al–Mg alloy coating in chloride-containing solution

Long‐term atmospheric corrosion rates of Zn55Al‐coated steel

Corrosion Behavior of Zinc-Aluminum-Magnesium Coated Steel in Simulated Marine Atmosphere

Study of the role of aluminium and corrosion mechanism in galvalume coating in the marine atmospheric environment

Investigation of the Corrosion Behavior of Zn-Al-Mg Hot-Dip Galvanized Steel in Alternating Climate Tests

Effect of Dipping Time on Microstructure and Properties of Zn-1Al-2Mg Coating by Hot-Dipping Galvanizing

Effects of Al content on microstructure and corrosion behavior of Zn-Al alloy coatings

Impact of cooling rates on the microstructure and cracking susceptibility of hot-dip galvanized Zn-12 wt% Al-5 wt% Mg coatings

Effect of SO2 and NH3 on the Corrosion Failure of Zn-Al-Mg Coatings

Characterisation of the galvanic protection of zinc flake coating by spectroelectrochemistry and industrial testing

Balanced Anti-Corrosion Action of Reduced Graphene Oxide in Zn-Al Coating during Medium-Term Exposure to NaCl Solution

Study on the structure and corrosion behavior of hot-dipped Zn–6Al–3Mg alloy coating in chlorine-containing environment

In-Situ Wettability Analysis of Al Coating Influence on Hot-Dip Galvanizing Properties of Advanced High-Strength Steels