Effect of dew point during heating on selective oxidation behavior of C-Mn-Si-Al high strength steel

Guangrui Jiang,Haiquan Wang,Libin Liu,Guanghui Liu

DOI: https://doi.org/10.13251/j.issn.0254-6051.2017.11.042

2017-01-01

Abstract:Many alloying elements , such as Si, Mn, Al, Cr and so on, are contained in advanced high strength steels , probably resulting in easier selective oxidation to form oxides on the surface of the steel during annealing and significant deterioration of the hot -dip galvanizing property.Effect of dew point during heating on the selective oxidation behavior of a C-Mn-Si-Al advanced high strength steel was studied on a hot-dip process simulator ( HDPS) .The surface morphology and composition distribution of as-annealed steel were analyzed by using SEM , EDS and GDOES .The results show that the external surface of the steel is covered by a large amount of nodule -shaped oxides , after annealed at the dew point (-10℃) during heating at higher temperature .With the dew point decreasing , the amount of the nodule-shaped oxides on the external surface reduces and even disappears .Moreover , with the dew point decreasing , enrichment of Mn on the external surface is weakened , while that of Al is promoted .