Abstract:The hot -dip 55 wt%Al-Zn-1.6 wt%Si-(0-3)wt.%Mg alloy coatings were experimentally investigated, and the solidification behaviors and hot cracking susceptibility were simulated by means of CALPHAD (CALculation of PHAse Diagrams) method. The scanning electron microscopy (SEM), electron probe micro -analyzer (EPMA) and glow discharge spectrometer method (GDS) were utilized to determine the microstructures and the distribution of elements of the Al-Zn-Mg alloy coatings with different Mg contents. It is discovered that with the increase of Mg content, the percentage of the eutectic microstructure scales up, and the surface quality of the alloy coating is improved. Meanwhile, the bending properties of Al-Zn-Mg coatings with different Mg contents still requires further improvement according to the present bending test. Subsequently, the equilibrium solidification processes of the coatings were calculated using thermodynamic approach. In general, the calculated results reflect the solidified phases and the precipitated temperatures according to theory of equilibrium solidification. However, there still exist discrepancies between the thermodynamic calculation results and the observed experimental results during the practical galvanizing process, because the cooling rates were not taken fully into consideration. Consequently, the kinetic analysis was carried out to obtain the secondary dendrite arm spacing under different cooling rates. The cracking susceptibility index (CSI) was also calculated to predict the hot workability of the Al-Zn-Mg alloy coating. In summary, the appropriate increase of the cooling rate turns out be the effective approach to benefit the microstructure and the corrosion resistance of the Al-Zn-Mg coatings in the practical galvanizing process, and the coating is not suitable for the hot stamping process.

Microstructural factors controlling crack resistance of Zn–Al–Mg alloy coatings prepared via hot-dip galvanizing process: Combined approach of in-situ SEM observation with digital image correlation analysis

Impact of cooling rates on the microstructure and cracking susceptibility of hot-dip galvanized Zn-12 wt% Al-5 wt% Mg coatings

Experimental Investigation and Kinetic Analysis of Al–Zn–Mg Alloy Coating

In-situ localization of damage in a Zn-Al-Mg coating deposited on steel by continuous hot-dip galvanizing

Microstructure of Hot-Dip Galvanized Zn-Al-Mg Alloy Coating

Micro Deformation Testing of Cast AM60B Mg Alloy Based on Scanning Electron Microscope and Digital Image Correlation Method

Nanoscale Investigation of Microcracks and Grain Boundary Wetting in Press Hardened Galvanized 20MnB8 Steel

Deformation and damage mechanisms of zinc coatings on hot-dip galvanized steel sheets: Part II. Damage modes

Crack generation, propagation mechanism and thermal property of Zn-coated hot stamping steel

Microstructure and Corrosion Resistance Property of a Zn-AI-Mg Alloy with Different Solidification Processes

Investigation of Microcracks on Conversion Film of AZ80 Mg Alloy

Improvement of cracking resistance of hot-dip Zn-Al-Mg coatings by heat treatment

Effect of Steel Composition and Processing Parameters on the Penetration Depth of Microcracks in ZnFe‐Coated Boron Steels

Revisiting the Cracking of Chemical Conversion Coating on Magnesium Alloys

Effects of Al-Mg on the Microstructure and Phase Distribution of Zn-Al-Mg Coatings

Roles of Al and Mg on the Microstructure and Corrosion Resistance of Zn-Al-Mg Hot-Dipped Coated Steel

Zn Diffusion and α -Fe(Zn) Layer Growth During Annealing of Zn-Coated B Steel

TEM Study on the Microstructure of the Zn-Al-Mg Alloy

Impact of Copper, Tin and Titanium Addition on Bending-Induced Damage of Intermetallic Phases in Hot Dip Galvanizing

Investigation of the LME Susceptibility of Dual Phase Steel with Different Zinc Coatings