Abstract:We report on our fabrication and characterization of Al2O3/Si composite nanodome (CND) structures, which is composed of Si nanodome structures with a conformal cladding Al2O3 layer to evaluate its optical and electrical performance when it is applied to thin film solar cells. It has been observed that by application of Al2O3 thin film coating using atomic layer deposition (ALD) to the Si nanodome structures, both optical and electrical performances are greatly improved. The reflectivity of less than 3% over the wavelength range of from 200 nm to 2000 nm at an incident angle from 0 degrees to 45 degrees is achieved when the Al2O3 film is 90 nm thick. The ultimate efficiency of around 27% is obtained on the CND textured 2 mu m-thick Si solar cells, which is compared to the efficiency of around 25.75% and 15% for the 2 mu m-thick Si nanodome surface-decorated and planar samples respectively. Electrical characterization was made by using CND-decorated MOS devices to measure device's leakage current and capacitance dispersion. It is found the electrical performance is sensitive to the thickness of the Al2O3 film, and the performance is remarkably improved when the dielectric layer thickness is 90 nm thick. The leakage current, which is less than 4x10(-9) A/cm(2) over voltage range of from -3 V to 3 V, is reduced by several orders of magnitude. C-V measurements also shows as small as 0.3% of variation in the capacitance over the frequency range from 10 kHz to 500 kHz, which is a strong indication of surface states being fully passivated. TEM examination of CND-decorated samples also reveals the occurrence of SiOx layer formed between the interface of Si and the Al2O3 film, which is thin enough that ensures the presence of field-effect passivation, From our theoretical and experimental study, we believe Al2O3 coated CND structures is a truly viable approach to achieving higher device efficiency. (C) 2015 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution 3.0 Unported License.

Optical and dielectric behavior of Al/CrO 3 /p-Si device

Investigation of electrical, dielectric and interface state densities of al/ p -Si structures with PTCDA interlayer under different light intensities

Highly Conductive p-Type Silicon Carbon Alloys Deposited by Hot-Wire Chemical Vapor Deposition

Electrical properties of Graphene/Silicon structure with Al2O3 interlayer

Electrical and optical characterization of SiONC dielectric thin film deposited by polymer-source chemical vapor deposition

Light-soaking Enhanced Passivation of Al2O3 on Crystalline Silicon Surface

Al 2 O 3 / NbAlO / Al 2 O 3 Sandwich Gate Dielectric Film on InP

Frequency and voltage-dependent dielectric spectroscopy characterization of Al/(Coumarin-PVA)/p-Si structures

Interface study of molybdenum oxide thin films on n- and p-type crystalline silicon surface

Study on the Properties of the Pc-Si Films Prepared by Magnetron Co-Sputtering at Low Temperature

Chromium Trioxide Hole-Selective Heterocontacts for Silicon Solar Cells

Ion implantation effects on the microstructure, electrical resistivity and thermal conductivity of amorphous CrSi2 thin films

Dual Function of Antireflectance and Surface Passivation of Atomic-Layer-Deposited $\hbox{al}_{2}\hbox{o}_{3}$ Films

Structural and optical properties of α-Si1-xCx:H thin films prepared by RF-PECVD

Electrical and Dielectric Behaviors of Al/SiO2-surfactant/n-Si Schottky Structure in Wide Range of Voltage and Frequency

Structural, Electronic, and optical properties of chromium oxynitride thin films grown by RF magnetron sputtering

Optical Properties of SiOx Film on Aluminum Substrate Prepared by APCVD

Study of Gamma-Ray Radiation Effects on the Passivation Properties of Atomic Layer Deposited Al2O3 on Silicon Using Deep-Level Transient Spectroscopy

Fabrication and characterization of Al2O3 /Si composite nanodome structures for high efficiency crystalline Si thin film solar cells

Investigation of the frequency effect on electrical modulus and dielectric properties of Al/p-Si structure with %0.5 Bi:ZnO interfacial layer

Investigation of dielectric and electric modulus properties of Al/p-Si structures with pure, 3%, and 5% (graphene:PVA) by impedance spectroscopy