Abstract:The 2195 Al-Li alloy, as one of the representative third-generation Al-Li alloys, has extensive applications in lightweight aerospace structures. In this paper, the anisotropy in mechanical properties and microstructure evolution of 2195 Al-Li alloy sheets were investigated under a strain rate of 0.01, 0.1, 1 s-1 and a temperature of 440 and 500 °C. Experimental results showed that the hot tensile properties of the 2195 Al-Li alloy sheet exhibited a strong dependence on loading directions. The peak stress (PS) and elongation (EL) along the rolling direction (RD) were larger than the transverse direction (TD). For the tests carried out at 440 °C-1 s-1, the PS values of the sheets stretched along the RD and TD are 142.9 MPa and 110.2 MPa, respectively. And, most of the PS anisotropy values are larger than 15%. The anisotropy in EL is less significant than in PS. All the differences are about 10%. Moreover, dimples in the samples stretched along RD were more and deeper than those along TD at 440 °C. The fracture morphology along RD and TD were similar, and both were cleavage fractures at 500 °C. Particularly, the fractions of high angle grain boundaries (HAGBs) along TD were all about 5% larger than those of RD. And, there were more small-sized continuous dynamic recrystallization (CDRX) grains inside the initial grains and discontinuous dynamic recrystallization (DDRX) grains featured with the local bulge of grain boundaries along TD. This was due to the smaller average Schmid factor and the vertical EL trend of the initial grains when the samples were stretched along TD. A model of grain evolution during the dynamic recrystallization (DRX) along RD and TD was proposed based on EBSD results. The Schmid factor and banded structure had a more prominent effect on the hot ductility of the 2195 Al-Li alloy compared with the degree of DRX, thus presenting a higher EL and better hot ductility along RD.

Balancing strength and ductility of LA141 alloy with a micro-nano laminated structure

The Evolution of Microstructure, Mechanical Properties and Fracture Behavior with Increasing Lanthanum Content in AZ91 Alloy

Microstructure and Mechanical Properties of Al-Mg-Si Similar Alloy Laminates Produced by Accumulative Roll Bonding

Achieving ultrahigh specific strength of an ultrafine grained Mg-9Li-1Al alloy via the combined processing of ECAP with repeated annealing and rolling

Effect of microalloying with rare-earth lanthanum on dynamic recrystallization behavior and mechanical properties of Ti sheets

Simultaneous Improvement of Strength, Ductility and Damping Capacity of Single Β-Phase Mg-Li-Al-Zn Alloys

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding

Microstructure and mechanical properties of wire-filled tungsten argon arc welded joints for LA141 magnesium-lithium-aluminum alloy

La drives the remarkable strength enhancement of the Cu-Cr-Zr alloy through traditional thermo-mechanical treatment

Enhancement of strength and ductility in 6061Al alloy processed by cross accumulative roll bonding

Preparation of bulk nanolaminated aluminum alloy with high strength

Interface behavior and tensile properties of Mg-14Li-3Al-2Gd sheets prepared by four-layer accumulative roll bonding

A high strength Al–Li alloy produced by laser powder bed fusion: Densification, microstructure, and mechanical properties

Effect of Initial Orientation on the Anisotropy in Microstructure and Mechanical Properties of 2195 Al-Li Alloy Sheet during Hot Tensile Deformation

Strong and ductile AZ31 Mg alloy with a layered bimodal structure

Microstructure evolution and mechanical behavior of α/β alternative Mg–Li alloy composite sheets with different initial thickness ratios prepared by accumulative roll bonding

Low-cost and high-strength Mg-Al-Ca-Zn-Mn wrought alloy with balanced ductility

Laser directed energy deposition remanufacturing of LPBF-processed TA15 parts: Hybrid process interface induced microstructure inheritance and mechanical performance

Novel isotropic mechanical properties of laser powder-bed fusion Sc/Zr modified Al alloy

Effect of La/Nd ratio on microstructure and tensile properties of AZ91-RE alloys

Effect of LaB6 on the Microstructure Evolution and Mechanical Properties of Ti-45Al-8Nb Alloy