Abstract:Grain size engineering, particularly reducing grain size into the nanocrystalline regime, offers a promising pathway to further improve the strength-to-weight ratio of Al alloys. Unfortunately, the fabrication of nanocrystalline metals often requires non-equilibrium processing routes, which typically limit the specimen size and require large energy budgets. In this study, multiple dopant elements in ternary Al alloys are deliberately selected to enable segregation to the grain boundary region and promote the formation of amorphous complexions. Three different fully dense bulk nanocrystalline Al alloys (Al-Mg-Y, Al-Fe-Y, and Al-Ni-Y) with small grain sizes were successfully fabricated using a simple powder metallurgy approach, with full densification connected directly to the onset of amorphous complexion formation. All the compositions demonstrate densities above 99% with grain sizes <60 nm following consolidation via hot pressing at 585 °C. The very fine grain structure results in excellent mechanical properties, as evidenced by nanoindentation hardness values in the range of 2.2-2.8 GPa. Detailed microstructural characterization verifies the segregation of all dopant species to grain boundaries as well as the formation of amorphous complexions, which suggests their influential role in aiding effective consolidation and endowing thermal stability in the alloys. Moreover, nanorods with a core-shell structure are also observed at the grain boundaries, which likely contribute to the stabilization of the grain structure while also strengthening the materials. Finally, intermetallic particles with sizes of hundreds of nanometers form in all systems. As a whole, the results presented here demonstrate a general alloy design strategy of segregation and boundary evolution pathway that enables the fabrication of multiple nanocrystalline Al alloys with hierarchical microstructures and improved performance.

Preparation of bulk nanolaminated aluminum alloy with high strength

Bulk Nanostructure Formation Directly From The Multicomponent Alloy Melt

Thermally Stable and Corrosion Resistant Nanolaminated Al-Mn Alloy with Low Angle Boundary Structures

Fabrications and mechanical properties of bulk amorphous, nanocrystalline, nanoquasicrystalline alloys in aluminum-based system

Mechanical properties and strengthening mechanism of Ni/Al nanolaminates: role of dislocation strengthening and constraint in soft layers

Processing of bulk nanolamellar tantalum and justification of strengthening by grain boundary pre-stressed model

Achieving ultrahigh specific strength of an ultrafine grained Mg-9Li-1Al alloy via the combined processing of ECAP with repeated annealing and rolling

Bulk nanocrystalline Al alloys with hierarchical reinforcement structures via grain boundary segregation and complexion formation

Deformation induced grain boundary segregation in nanolaminated Al–Cu alloy

Hierarchical nanostructured aluminum alloy with ultrahigh strength and large plasticity

Bulk Nanocrystalline High-Strength Magnesium Alloys Prepared Via Rotary Swaging

Achieving ultrahigh strength in binary Al-10Mg alloy through heavy cryogenic rolling

Approaching 1 GPa ultra‐high tensile strength in a nanostructured Al‐Zn‐Mg‐Cu‐Zr‐Sc alloy prepared by severe plastic deformation

Additive manufacturing of an ultrastrong, deformable Al alloy with nanoscale intermetallics

Bulk nanostructured Al-Si alloy with remarkable improvement in strength and ductility

Microstructural evolution and mechanical properties of Ni/Al reactive nanolaminates with different NixAly intermetallic phases

Achieving superior strength and ductility in 7075 aluminum alloy through the design of multi-gradient nanostructure by ultrasonic surface rolling and aging

Novel approach to additively manufacture high-strength Al alloys by laser powder bed fusion through addition of hybrid grain refiners

Microstructure and properties of a novel ultra-high strength, high elasticity and high plasticity Cu–20Ni–20Mn-0.3Nb-0.3Cr-0.1Zr alloy

Fabrication of Nanocrystalline High‐Strength Magnesium−Lithium Alloy by Rotary Swaging

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations