Abstract:In this paper, "bimodal microstructure" and enhanced mechanical properties of extruded Mg-Gd-Y-Zn-Zr alloy is achieved by regulating the initial long-periodic stacking-ordered (LPSO) phases, the effect of blocky LPSO phase and lamellar LPSO phase on the dynamic recrystallization (DRX) behavior and the formation mechanism of bimodal microstructure are systematically investigated, the deformation modes, strengthening and toughening mechanism and fracture behavior of the "bimodal microstructure" are analyzed by slip traces. Blocky LPSO phase has significant particle stimulated nucleation (PSN) effect to promote DRX. The effect of lamellar LPSO phase on DRX depends on the size, fragmented lamellar LPSO with small size promotes numerous DRXed grains through the PSN effect, while continuous intragranular lamellar LPSO with large size inhibits DRX by hindering slip and grain boundary rotation, which is the key factor to form the bimodal microstructure. The almost fully DRXed H510 sample has the lowest strength, and the H-525 sample with "bimodal microstructure" achieves enhanced comprehensive mechanical properties (ultimate tensile strength, yield strength and elongation of 383 MPa, 308 MPa and 9.2 %, respectively), which is related to the significant texture strengthening and dislocation strengthening of large-sized unDRXed grains, as well as strain coordination of higher DRXed grains fraction. The deformation mode of the DRXed regions is grain boundary sliding, while the unDRXed regions are dominated by prismatic slip, the strain incompatibility between the two is the decisive factor causing microcracks propagation and final fracture. This paper will provide theoretical guidance for the initial microstructure design of strengthplasticity synergistic Mg-Gd-Y-Zn-Zr alloys with bimodal microstructure.

Strong and ductile AZ31 Mg alloy with a layered bimodal structure

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Strength-ductility balance of AZ31 magnesium alloy via accumulated extrusion bonding combined with two-stage artificial cooling

Microstructure, Texture and Mechanical Properties of AZ31 Magnesium Alloy Fabricated by High Strain Rate Biaxial Forging

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

Ductility enhancement mechanism of AZ31 magnesium alloy with through-thickness symmetrical gradient structure prepared by hard plate rolling

High strength-ductility synergy and low anisotropy of Mg-4.5Al-2.6Zn-0.3Mn alloy sheet achieved by annealing after rolling

Tailoring bimodal grain structure of Mg-9Al-1Zn alloy for strength-ductility synergy: Co-regulating effect from coarse Al2Y and submicron Mg17Al12 particles

Influence of bimodal microstructure on strength and ductility of as-extruded Mg-Gd-Y-Zr alloy

Interfacial Bonding and Fracture Behaviors of AZ63 Magnesium Alloy Sheet Processed by Accumulative Roll Bonding

Enhancing grain refinement and mechanical properties of AA1100/MgAZ31/AA1100 composites by using different roll bonding techniques

Achieving Enhanced Mechanical Properties of Extruded Mg-Gd-Y-Zn-Zr Alloy by Regulating the Initial LPSO Phases

Microstructure, texture and mechanical properties of the rolled high modulus Mg-Y-Zn-Al-Li alloy

Effect of a bimodal grain structure on corrosion behavior and tensile properties of low-alloyed Mg-1Bi-1Zn-1Ag alloy

Achieving high strength near 400 MPa in an ultra-fine grained Mg–Bi–Ca ternary alloy via low-temperature extrusion

A Rolled Mg‐8Al‐1Sm‐1Zn Alloy with High Strength‐Ductility via Single‐Pass Liner Rolling

Microstructure evolution and mechanical behavior of α/β alternative Mg–Li alloy composite sheets with different initial thickness ratios prepared by accumulative roll bonding

Microstructure and Mechanical Properties of AZ31B Magnesium Alloy via Ultrasonic Surface Rolling Process

Effect of annealing treatment on the microstructure and mechanical properties of warm-rolled Mg–Zn–Gd–Ca–Mn alloys

Microstructures and Mechanical Properties of a High-Strength Mg-3.5Sm-0.6Zn-0.5Zr Alloy