Abstract:Ultrasonic surface rolling processing (USRP) was performed on a Mg–Y–Nd–Zr alloy after equal-channel angular pressing. The result shown that the surface roughness was significantly improved, residual stress was introduced to the topmost surface, and ~450 μm gradient nanostructure (GNS) of Mg alloys was obtained after USRP treatment. The mechanism of microstructure evolution and its effect on the mechanical properties of the Mg alloy were studied in detail. There are multiple deformation mechanisms in grain refinement. In the initial stage, the coarse-grain (CG) matrix was subdivided by {10 1̅ 2} extension twins. Subsequently, the deformed grains were refined into substructures using interaction between twins, interaction between twins and dislocations, and dislocation entanglement. Moreover, the substructure contains a high density of multiple stacking faults and dislocation arrays, which can effectively block dislocation movement and promote dislocation packing. Finally, equiaxed nanograins (NGs) with high-angle grain boundaries were formed via subcrystal rotation recrystallization. With the formation of a GNS, the strength of the Mg–Y–Nd–Zr alloy considerably increased at the expense of a small amount of plasticity. The tensile test results demonstrated that the yield strength (YS) and ultimate tensile strength (UTS) of the Mg–Y–Nd–Zr alloy increased from 171.96 and 262.47 MPa to 216.06 and 330.61 MPa, respectively, and the elongation rate decreased from 20.52% to 14.65% after the USRP treatment. The YS improvement of the Mg–Y–Nd–Zr alloy after the USRP treatment was attributed to grain boundary strengthening, synergistic strengthening, dislocation strengthening, and twin strengthening. Furthermore, the microhardness of Mg–Y–Nd–Zr considerably improved after USRP treatment, and grain refinement was the primary surface strengthening mechanism of the Mg–Y – Nd – Zr alloy after the USRP treatment. The work-hardening capacity of the Mg alloy improved after the USRP treatment, and the synergistic deformation between GNS and CG matrix was the primary reason for the excellent work-hardening capacity of the Mg–Y–Nd–Zr alloy.

Microstructure and Mechanical Properties of AZ31B Magnesium Alloy via Ultrasonic Surface Rolling Process

Effect of ultrasonic surface rolling process on mechanical properties and corrosion resistance of AZ31B Mg alloy

Microstructures and mechanical properties of Mg-15Gd-1Zn-0.4Zr alloys treated by ultrasonic surface rolling process

Effect of ultrasonic surface rolling process on microstructure and properties of rolled Mg-Y-Nd-Zr alloy

Effect of microstructure evolution on the mechanical properties of a Mg–Y–Nd–Zr alloy with a gradient nanostructure produced via ultrasonic surface rolling processing

Formation Mechanism of Surface Gradient Microstructure and Mechanical Properties Evolution of Mg-Y-Nd-Gd-Zr Alloy by Ultrasonic Rolling

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Simultaneously improving mechanical properties and corrosion resistance of as-cast AZ91 Mg alloy by ultrasonic surface rolling

Mechanical Properties and Texture Evolution During Rolling Process of an AZ31 Mg Alloy

Microstructure And Mechanical Properties Of Az31 Magnesium Alloy Sheet By Hot Rolling

Recrystallization and Anisotropy of AZ31 Magnesium Alloy by Asynchronous Rolling

Microstructure Evolution and Mechanical Properties of AZ31 Alloy with Accumulative Roll Bonding

Evolution of the Microstructure and Mechanical Properties of AZ31 Magnesium Alloy Sheets during Multi-Pass Lowered-Temperature Rolling

Microstructure, Texture Evolution, and Mechanical Properties of Thin AZ31B Mg Alloy Sheets Prepared by Two-Stage Rolling

Microstructure and Mechanical Properties of an Asymmetric Twin-Roll Cast Az31 Magnesium Alloy Strip

Effect of Symmetric and Asymmetric Rolling Processes on The Microstructure and Mechanical Properties of AZ31B Magnesium Alloy

Effect of rolling reduction on microstructure, texture, mechanical properties and mechanical anisotropy of AZ31 magnesium alloys

The improvement on mechanical anisotropy of AZ31 magnesium alloy sheets by multi cross-rolling process

Influence of Microstructure and Mechanical Properties on Formability in High Strain Rate Rolled AZ31 Magnesium Alloy Sheets

Effect of Asymmetric Cross Rolling on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Obtaining Heterogeneous Microstructure and Enhanced Mechanical Properties in ECAP-Processed AZ61 Alloys via Single-Pass Rolling with Increased Rolling Reduction