Effects of Ultrasonic Surface Rolling Processing and Subsequent Recovery Treatment on the Wear Resistance of AZ91D Mg Alloy

Xiaohui Zhao,Kaichao Liu,Desheng Xu,Yu Liu,Chunhua Hu
DOI: https://doi.org/10.3390/ma13245705
IF: 3.4
2020-12-14
Materials
Abstract:AZ91D Mg alloy was treated by ultrasonic surface rolling processing (USRP) and subsequent recovery treatment at different temperatures. The dry sliding friction test was performed to investigate the effects of USRP and subsequent recovery treatment on the wear resistance of AZ91D Mg alloy by a ball-on-plate tribometer. The microstructure, properties of plastic deformation layer and worn morphology were observed by optical microscope (OM), scanning electron microscope (SEM), transmission electron microscope (TEM), X-ray diffraction (XRD) analysis and microhardness tester. Results illustrate that the grains of AZ91D Mg alloy surface layer are refined to nanocrystallines. The maximum microhardness of the top surface of the USRP sample reaches 102.3 HV. When USRP samples are treated by recovery treatment at 150 °C, 200 °C and 250 °C, the microhardness of the top surface decreases to 90.68 HV, 79.29 HV and 75.06 HV, respectively. The friction coefficient (FC) and wear volume loss of the USRP-R-150 sample are the lowest among all the samples. The worn surface morphology of the USRP-R-150 sample is smoother than that of other samples, indicating that the wear resistance of AZ91D Mg alloy treated by USRP and recovery treatment at 150 °C is improved significantly.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The problem that this paper attempts to solve is the application limitations of magnesium alloy AZ91D in applications due to its poor wear resistance. Specifically, the research aims to improve the wear - resistant properties of AZ91D magnesium alloy through ultrasonic surface rolling process (USRP) and subsequent recovery heat treatment. The research focuses on the influence of recovery treatment at different temperatures on the surface microstructure and wear - resistant properties of the material, in order to find the optimal treatment conditions and thus significantly improve the wear resistance of the material. The paper experimentally compared the friction coefficient and wear volume loss of the original sample, the sample only treated by USRP, and the samples after recovery treatment at different temperatures under dry sliding friction conditions, and analyzed the effects of these treatment methods on the surface hardness of the material, microstructure changes and their influence on the wear - resistant properties. The research shows that USRP treatment can significantly refine the grains in the surface layer of the material to the nanometer level and increase the surface hardness; after the recovery treatment at 150 °C, the material not only maintains a high surface hardness, but also further improves its wear - resistant properties, showing the lowest friction coefficient and wear volume loss, indicating that the wear resistance of the material is significantly enhanced under this condition. This provides an important reference basis for the practical application of magnesium alloys.