Highly permeable polyethersulfone substrates with bicontinuous structure for composite membranes in CO2/N2 separation

Ruizhi Pang,Kai K. Chen,Yang Han,W.S. Winston Ho
DOI: https://doi.org/10.1016/j.memsci.2020.118443
IF: 9.5
2020-10-01
Journal of Membrane Science
Abstract:<p>Substrate morphology has a significant effect on the CO<sub>2</sub> transport performance of a thin-film composite (TFC) membrane. In this study, a new mixed solvent comprising 2-pyrrolidone (2-PD) and 2-methoxyethanol (2-ME) was used to prepare polyethersulfone (PES) substrates with bicontinuous structure by water vapor-induced phase separation, followed by immersion in water as nonsolvent. Compared with the commonly used solvent, <em>N</em>-methyl-2-pyrrolidone (NMP), the 2-PD/2-ME mixed solvent is more hydrophilic and can decrease the thermodynamic stability of the casting solution significantly. As a result, the phase separation was induced via the spinodal decomposition mechanism. The open morphology bestowed the optimized substrate with a very high CO<sub>2</sub> permeance of 133,226 ± 3870 GPU (1 GPU = 10<sup>–6</sup> cm<sup>3</sup>(STP) s<sup>–1</sup> cm<sup>–2</sup> cmHg<sup>–1</sup> = 3.3464 × 10<sup>-9</sup> kg-mol s<sup>–1</sup> m<sup>–2</sup> Pa<sup>–1</sup>), which was 5 times more permeable than the baseline substrate synthesized with NMP. By using this new substrate, the prepared TFC membrane containing amines showed an increased CO<sub>2</sub> permeance of 908 ± 8 GPU at 57 °C, which was 48 GPU higher than that with the baseline substrate. Meanwhile, the CO<sub>2</sub>/N<sub>2</sub> selectivity was retained at 162 ± 4 at 57 °C. In addition, the good scalability of the new PES substrate was demonstrated by roll-to-roll fabrication of a 50′ long scale-up PES substrate with a width of 21ʺ.</p>
engineering, chemical,polymer science
What problem does this paper attempt to address?