Unveiling the Potential: Core‐Shell Nanoparticles Assembly of Metal‐Organic Framework@poly(1,3‐dioxolane) Methacrylate for Gutter‐Layer‐Free Ultrathin Film Composite Membranes
Hoseong Han,Joel M. P. Scofield,Paul A. Gurr,Paul A. Webley,Greg G. Qiao
DOI: https://doi.org/10.1002/admi.202400113
IF: 5.4
2024-06-24
Advanced Materials Interfaces
Abstract:The core‐shell architectures, utilizing robust metal‐organic frameworks (MOFs) as core initiators and poly(1,3‐dioxolane) dimethacrylate (PDXLMA) as shell materials, are synthesized to produce an ultrathin two‐layered composite membrane without the requirement for gutter layers. The resulting defect‐free membranes show exceptional gas separation performance, achieving a CO2 permeance of up to 6,035 GPU while maintaining a CO2/N2 selectivity of >20. Increasing amounts of carbon dioxide (CO2) emissions in the atmosphere are a leading cause of climate change. Ultrathin film composite (UTFC) membranes have the potential to effectively reduce CO2 emissions from energy production and industrial processes. UTFC membranes typically require a gutter layer, to provide flat surfaces above the porous substrate for an ultrathin selective layer to be deposited. Removing the gutter layer, while maintaining compatibility with the support layer, can have substantial benefits of high gas permeation, cost‐effectiveness, and fewer manufacturing steps. However, achieving this faces significant challenges, due to limitations on the geometric design of gas pathways and incompatibility between the substrate and selective layers. Herein, zeolitic imidazolate framework‐8 (ZIF‐8) is used as an initiating core, and arms of poly(1,3‐dioxolane) dimethacrylate (PDXLMA), which possesses superior CO2/N2 selectivity, are used to create core‐shell nanoparticles. These two‐layered UTFC membranes are successfully produced from the nanoparticles via a simple drop‐spreading method. The importance of designing core‐shell structures is also investigated to achieve defect‐free two‐layered UTFC membranes and enable precision thickness control. The resulting membranes exhibit remarkable CO2 permeance of 3969 – 6035 GPU with CO2/N2 selectivity of 28.0–20.4, demonstrating their considerable performance improvement compared to the current three‐layered UTFC membranes.
materials science, multidisciplinary,chemistry