Abstract:Preparation of CO2 separation membrane with high gas permeance and CO2 selectivity is always desirable. In this work, inspired by pesticides and cosmetics, through the use of a variety of additives, good compatibility between the water-based coating solution of low concentration and the hydrophobic surface of the intermediate layer (or gutter layer) had been achieved. A membrane with high gas permeance and moderate CO2 selectivity was prepared preliminarily, and the synergistic mechanism among various additives was clarified. Then, through simple cross-linking modification of the membrane surface, a multi-layer composite membrane for CO2 separation was prepared with CO2 selectivity being improved greatly. The degree of cross-linking on the membrane surface and the thickness of the cross-linked layer was studied by XPS etching analysis. Separation performance for CO2/N2, CO2/CH4, and CO2/H2 mixture had been tested, and the prepared multi-layer composite membrane exhibited excellent CO2 separation performance. Moreover, the simulated flue gas test showed that the prepared membrane was of good long-term stability and impurity resistance.

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to develop a high - performance multi - layer composite membrane to achieve efficient carbon dioxide separation. Specifically, the research aims to improve the gas permeability and carbon dioxide selectivity of the membrane by enhancing the compatibility between each layer and surface cross - linking. The following are the main focuses of the paper: 1. **Improving gas permeability and carbon dioxide selectivity**: The goal of the paper is to prepare a multi - layer composite membrane with high gas permeability and moderate carbon dioxide selectivity. To achieve this goal, the researchers improved the compatibility between the water - based coating solution and the hydrophobic surface of the intermediate layer (or groove layer) by using multiple additives. 2. **Solving the compatibility problem of membrane materials**: Many materials with high carbon dioxide permeability and selectivity are hydrophilic or contain alcohol groups, while the intermediate layer materials are usually hydrophobic. Therefore, how to achieve good compatibility between these materials is a key issue. The paper achieved good compatibility between the hydrophilic separation layer and the hydrophobic intermediate layer by referring to the additives used in pesticides and cosmetics. 3. **Surface cross - linking modification**: The carbon dioxide selectivity of the membrane was further improved through simple surface cross - linking modification. The researchers studied the cross - linking degree of the membrane surface and the thickness of the cross - linking layer through XPS etching analysis. 4. **Long - term stability and anti - impurity ability**: The paper also tested the long - term stability and anti - impurity ability of the prepared multi - layer composite membrane in simulated flue gas, and the results showed that the membrane has good long - term stability and anti - impurity ability. In summary, this paper mainly solves the following problems: - How to prepare a multi - layer composite membrane with high gas permeability and carbon dioxide selectivity. - How to improve the compatibility between the hydrophilic separation layer and the hydrophobic intermediate layer through additives. - How to further improve the carbon dioxide selectivity of the membrane through surface cross - linking modification. - How to ensure the long - term stability and anti - impurity ability of the membrane in practical applications.

High-performance multi-layer composite membrane with enhanced interlayer compatibility and surface crosslinking for CO2 separation

Selective Permeation of CO2 Through a Composite Membrane with a Separation Layer of 2-N,n-dimethyl Aminoethyl Methacrylate and Acrylic Acid Copolymer

Ultrahigh Carbon Dioxide-Selective Composite Membrane Containing a γ-CD-MOF Layer

Hybrid Organosilica Membrane with High CO2 Permselectivity Fabricated by a Two-Step Hot Coating Method

Preparation of a PVA/Chitosan/Glass Fiber Composite Membrane and the Performance in CO2 Separation

Stiff Metal–organic Framework–polyacrylonitrile Hollow Fiber Composite Membranes with High Gas Permeability

Preparation and Separation Performance of PDMS Composite Membranes for CO2 Separation from CO2-DMC System

Preparation of a novel dual-layer polyvinylidene fluoride hollow fiber composite membrane with hydrophobic inner layer for carbon dioxide absorption in a membrane contactor

High-efficiency CO2 separation using hybrid LDH-polymer membranes

Large-scale preparation of multilayer composite membranes for post-combustion CO2 capture

Enhanced CO 2 Separation by Functionalized g-C 3 N 4 Nanosheets as Composite Filler to Fabricate Mixed Matrix Membranes

Heteroatom-doped noble carbons tailored mixed matrix membrane with ultrapermeability for efficient CO2 separation

Selective membrane separation of CO2 using novel epichlorohydrin-amine-based crosslinked protic ionic liquids: Crosslinking mechanism and enhanced salting-out effect

Performance of Multilayer Composite Hollow Membrane in Separation of CO2 from CH4 in Mixed Gas Conditions

Mixed matrix composite membranes with MOF-protruding structure for efficient CO 2 separation

Construction of high-performance thin-film composite membrane for CO 2 separation via interface engineering

Development of cost-effective cellulose-based bilayer hybrid composite membranes for CO2 separation in biogas purification

Self‐Standing Covalent Organic Framework Membranes for H2/CO2 Separation

Highly permeable polyethersulfone substrates with bicontinuous structure for composite membranes in CO2/N2 separation

Fabrication of polyarylate thin-film nanocomposite membrane based on graphene quantum dots interlayer for enhanced gas separation performance

Covalent organic frameworks-incorporated thin film composite membranes prepared by interfacial polymerization for efficient CO2 separation