Abstract:A novel method based on the aluminothermic reduction of TiO 2 in Na 3 AlF 6 -AlF 3 -CaF 2 molten salts has been proposed to prepare Al-Ti intermetallic alloys in this research. The Al-Ti intermetallic alloy was obtained by reducing dissolved TiO 2 in electrolyte molten salt using liquid Al as a reductant at the stirring rate of 200 r/min for 5 min under 960°C, and it was mainly enriched in the Al matrix which was dispersed in molten salts. The lower alloy layers in the melt pool were characterised by X-ray diffraction (XRD), scanning electron microscopy, energy dispersive spectroscopy (SEM-EDS), and X-ray photoelectron spectroscopy (XPS), taking advantage of the specific gravity difference between the molten salt and the alloy. The TiAl 3 was the major intermetallic alloys phase formed between Al and Ti according to XRD results. The Al 2 O 3 by-product in the reduction process of TiO 2 was dissolved in electrolyte molten salt. Dans cette recherche, on a proposé une nouvelle méthode basée sur la réduction aluminothermique de TiO 2 dans des sels fondus de Na 3 AlF 6 -AlF 3 -CaF 2 pour préparer des alliages intermétalliques Al-Ti. On a obtenu l'alliage intermétallique Al-Ti en réduisant du TiO 2 dissous dans l'électrolyte de sels fondus en utilisant l'Al liquide comme réducteur à la vitesse d'agitation de 200 tr/min pendant 5 min à 960°C, et il a été principalement enrichi dans la matrice d'Al, qui a été dispersée dans les sels fondus. On a caractérisé les couches inférieures d'alliage dans le bain de fusion, par diffraction des rayons X (XRD), microscopie électronique à balayage et spectroscopie à dispersion d'énergie (SEM-EDS) et spectroscopie de photoélectrons (XPS), prenant avantage de la différence de densité relative entre le sel fondu et l'alliage. Le TiAl 3 était la phase majeure d'alliages intermétalliques formée entre Al et Ti selon les résultats de XRD. Le sous-produit Al 2 O 3 du procédé de réduction du TiO 2 a été dissous dans l'électrolyte de sels fondus, puis Al a pu être récupéré par réduction électrolytique, ce qui peut réaliser le recyclage de l'aluminium métallique. Le procédé de réduction aluminothermique a fourni une méthode métallurgique à productivité élevée et sans pollution pour préparer l'alliage intermétallique Al-Ti.

Fabrication of U-Ti alloy through direct electro-reduction from U3O8 and TiO2 mixtures in LiCl molten salt

Electrochemical Behavior and Reduction of UO22+ in LiCl-KCl Molten Salt

Preparation of Γ-Uranium-molybdenum Alloys by Electrochemical Reduction of Solid Oxides in LiCl Molten Salt

Synthesis of micro-FeTi powders by direct electrochemical reduction of ilmenite in CaCl2-NaCl molten salt

Chemical Species Transformation During the Dissolution Process of U3O8 and UO3 in the LiCl-KCl-AlCl3 Molten Salt

Electrochemical extraction of titanium from carbon-doped titanium dioxide precursors by electrolysis in chloride molten salt

Direct electrochemical reduction of low titanium chlorides into titanium aluminide alloy powders from molten eutectic KCl–LiCl–MgCl2

Fabrication of Al-Ti intermetallic alloy via aluminothermic reduction process from TiO2 in molten salts

Chemical Species Transformation during the Dissolution Process of U 3 O 8 and UO 3 in the LiCl–KCl–AlCl 3 Molten Salt

A Liquid Alloy Anode for the Electrolytic Reduction of Uranium Oxide in Molten Lithium Chloride

Electrochemical recovery of UO2 from LiCl-KCl-UO2F2 molten salt

Electrochemical synthesis of Ti–Al–V alloy by chlorination of Ti2O3 and V2O3 in AlCl3-containing molten chloride salt

Investigation on the reaction progress of titanium and lead chloride in NaCl-KCl melt

Study on the electrodeposition of uranium in chloride molten salt

Studies on the Electrodeposition of UO 2 Production in UO 2 Cl 2 -LiCl-KCl Melt

Direct Electro-deoxidation of Ilmenite Concentrate to Prepare FeTi Alloy in CaCl2 Molten Salt

Sustainable recycling of titanium scraps and purity titanium production via molten salt electrolysis

Preparation of Ferrotitanium Alloy from Ilmenite by Electrochemical Reduction in Chloride Molten Salts

Composition and structure of Ti–Al alloy powders formed by electrochemical co-deposition in KCl–LiCl–MgCl2–TiCl3–AlCl3 molten salt

Uranium chemical species in LiCl-KCl eutectic under different conditions for the dissolution of U3O8