Electrochemical recovery of UO2 from LiCl-KCl-UO2F2 molten salt

Wei Han,Xinyao Feng,Yijie Wang,Rugeng Liu,Meng Zhang,Mei Li

DOI: https://doi.org/10.1016/j.seppur.2022.122965

IF: 8.6

2023-03-01

Separation and Purification Technology

Abstract:To recover UO2 from LiCl-KCl-UO2F2 molten salt, the electrochemical behavior of UO 2 2 + and nucleation mechanism of UO2 were studied by a series of electrochemical techniques. The results of cyclic voltammetry and square wave voltammetry showed that UO2 was formed through two-step reduction process of UO 2 2 + involving one electron transfer. The disproportionation reaction of UO 2 + was investigated by calculating electric charge, demonstrating the disproportionation reaction occurred as 2 UO 2 + = UO 2 + UO 2 2 + . The exchange current densities of UO 2 + / UO 2 couple were determined at various temperatures by Tafel technique, and their values increased with the increasing temperature, which was in accordance with the Arrhenius equation, therefore, the activation energy of the reaction was estimated to be 32.31 kJ mol−1. Meanwhile, the nucleation mechanism of UO2 was investigated to follow the progressive nucleation by chronoamperometry. Furthermore, potentiosatic electrolysis was performed at various applied potentials, and the results indicated that UO2 had a regular octahedral microstructure, and the applied potential affected the size of UO2 crystal. In addition, UO2 was prepared by pulse electrolysis at 2.02 V in duty ratios of 75 % and 60 %, the results of SEM showed that pulse electrolysis could avoid the formation of dendrite.

engineering, chemical