Abstract:The processes of cathodic reduction of U(III) ions to metal in a low–melting LiCl–KCl–CsCl eutectic at the temperature range 650–850 K on tungsten, gallium and cadmium electrodes in an inert gas atmosphere have been studied by non-stationary and stationary electrochemical methods. Reagents without contain impurities of moisture, oxygen and their compounds were used in the experiments. All major operations were performed in a dry glove box. The following methods were used to analyze the electrochemical processes: cyclic voltammetry, square-wave voltammetry and potentiometry at zero current. On cyclic voltammogram of the molten LiCl–KCl–CsCl–UCl3 solution on an inert tungsten electrode, one cathode current peak corresponding to the deposition of metallic uranium and one anode current peak associated with its dissolution were recorded. It was found that the potential of the cathode peak was shifted to a region of more negative values with an increase of the scan rate. The value of the cathode peak current was directly proportional vs. the square root of the polarization rate, but this dependence does not pass through the origin. Consequently, the system of U(III)/U(0) couple was irreversible and proceeds in one stage. It was found that on square-wave voltammograms in the studied “electrochemical window” the deposition of uranium on liquid reactive gallium and cadmium electrodes was carried out at more positive values than on inert tungsten electrode. It was established that this potential shift was associated with the formation of intermetallic compounds of uranium with the material of reactive electrodes. The values of the alloy formation potentials were determined. For identification of the composition of cathode deposits, potentiostatic electrolysis was performed. By X–ray diffraction analysis, it was found that the formation of the intermetallic compounds Ga3U and Ga2U occurs on the gallium reactive electrode, and Cd11U occurs on the cadmium one. The conditions of their formation during the electrolysis of molten LiCl–KCl–CsCl–UCl3 solutions were established. The reaction of the electrochemical extraction of uranium from molten LiCl–KCl–CsCl–UCl3 electrolyte was investigated on liquid reactive electrodes at different duration of electrolysis. It was found that the electrochemical extraction of uranium exceeds 97% on both Ga and Cd electrodes.

Impact of Ag on Electrochemical Recovery of UO 2 in Molten LiCl-KCl Salt

Electrochemical recovery of UO2 from LiCl-KCl-UO2F2 molten salt

Studies on the Electrodeposition of UO 2 Production in UO 2 Cl 2 -LiCl-KCl Melt

Electrochemical Behavior and Reduction of UO22+ in LiCl-KCl Molten Salt

Study on the electrodeposition of uranium in chloride molten salt

Electrocrystallization of UO2 on nanoporous WO3/W electrode in LiCl-KCl melts

The Electrode Kinetics of UCl3 in LiCl-KCl Molten Salt

Insight into the influence mechanism of chloride ions towards in-situ electric-induced uranium incorporation into magnetite

ELECTROCHEMICAL SYNTHESIS OF INTERMETALLIC U–Ga AND U–Cd COMPOUNDS IN MOLTEN LiCl–KCl–CsCl EUTECTIC

Identification, Measurement, and Mitigation of Key Impurities in LiCl-Li2O Used for Direct Electrolytic Reduction of UO2

Chemical Species Transformation During the Dissolution Process of U3O8 and UO3 in the LiCl-KCl-AlCl3 Molten Salt

Uranium chemical species in LiCl-KCl eutectic under different conditions for the dissolution of U3O8

Electrodeposition of AgCuO2 Nanoplates

Electrochemical Properties of Uranium on the Liquid Gallium Electrode in Licl-Kcl Eutectic

Separation of U4+/UO22+ from the Chloride Molten Salts with Microplasma Gaseous Anodes

Chemical Species Transformation during the Dissolution Process of U 3 O 8 and UO 3 in the LiCl–KCl–AlCl 3 Molten Salt

A recovery technology of Ag from composite Ag-Cu electronic wastes

Cathode processes and uranium electrochemical extraction on W and Ga electrodes in LiCl–KCl melt

Electrochemical Electron Transfer and Crystallization Process of Uranium (vi) in Sodium Salt Solution

A Particularly Simple NH4Cl-based Method for the Dissolution of UO2 and Rare Earth Oxides in LiCl-KCl Melt under Air Atmosphere

Uranium elimination and recovery from wastewater with ligand chelation-enhanced electrocoagulation