Abstract:The processes of cathodic reduction of U(III) ions to metal in a low–melting LiCl–KCl–CsCl eutectic at the temperature range 650–850 K on tungsten, gallium and cadmium electrodes in an inert gas atmosphere have been studied by non-stationary and stationary electrochemical methods. Reagents without contain impurities of moisture, oxygen and their compounds were used in the experiments. All major operations were performed in a dry glove box. The following methods were used to analyze the electrochemical processes: cyclic voltammetry, square-wave voltammetry and potentiometry at zero current. On cyclic voltammogram of the molten LiCl–KCl–CsCl–UCl3 solution on an inert tungsten electrode, one cathode current peak corresponding to the deposition of metallic uranium and one anode current peak associated with its dissolution were recorded. It was found that the potential of the cathode peak was shifted to a region of more negative values with an increase of the scan rate. The value of the cathode peak current was directly proportional vs. the square root of the polarization rate, but this dependence does not pass through the origin. Consequently, the system of U(III)/U(0) couple was irreversible and proceeds in one stage. It was found that on square-wave voltammograms in the studied “electrochemical window” the deposition of uranium on liquid reactive gallium and cadmium electrodes was carried out at more positive values than on inert tungsten electrode. It was established that this potential shift was associated with the formation of intermetallic compounds of uranium with the material of reactive electrodes. The values of the alloy formation potentials were determined. For identification of the composition of cathode deposits, potentiostatic electrolysis was performed. By X–ray diffraction analysis, it was found that the formation of the intermetallic compounds Ga3U and Ga2U occurs on the gallium reactive electrode, and Cd11U occurs on the cadmium one. The conditions of their formation during the electrolysis of molten LiCl–KCl–CsCl–UCl3 solutions were established. The reaction of the electrochemical extraction of uranium from molten LiCl–KCl–CsCl–UCl3 electrolyte was investigated on liquid reactive electrodes at different duration of electrolysis. It was found that the electrochemical extraction of uranium exceeds 97% on both Ga and Cd electrodes.

The Electrode Kinetics of UCl3 in LiCl-KCl Molten Salt

Electrochemical Behavior and Reduction of UO22+ in LiCl-KCl Molten Salt

Electrochemistry of Uranium on Liquid Cadmium Electrode in LiCl-KCl Eutectic

The Application of Low-Melting LiCl-KCl-CsCl Eutectic to Electrodeposit Uranium Metal

Uranium chemical species in LiCl-KCl eutectic under different conditions for the dissolution of U3O8

Initial Nucleation and Growth Morphology of Uranium Electrodeposited in LiCl-KCl Eutectic

Reaction Behavior and Mechanism of Uranium Metal with ZnCl2 in LiCl-KCl Eutectic Molten Salt

Cathode processes and uranium electrochemical extraction on W and Ga electrodes in LiCl–KCl melt

ELECTROCHEMICAL SYNTHESIS OF INTERMETALLIC U–Ga AND U–Cd COMPOUNDS IN MOLTEN LiCl–KCl–CsCl EUTECTIC

Electrochemical Extraction of Uranium from U3O8 by Preparing Flower-Shaped Al-U Intermetallics in LiCl-KCl-AlCl3 Melts.

The influence of F− ion on the electrochemical behavior and coordination properties of uranium in LiCl-KCl molten salt

Confirmation and elimination of cyclic electrolysis of uranium ions in molten salts

Electrochemical Drawdown of U 3+ and Ce 3+ in Molten LiCl-KCl Using a Liquid Cadmium Cathode

Electrochemical Drawdown of U3+ and Ce3+ in Molten LiCl-KCl Using a Liquid Cadmium Cathode

Study on the electrodeposition of uranium in chloride molten salt

Electrochemical Properties of Uranium on the Liquid Gallium Electrode in Licl-Kcl Eutectic

Studies on the Electrodeposition of UO 2 Production in UO 2 Cl 2 -LiCl-KCl Melt

Electrochemical Electron Transfer and Crystallization Process of Uranium (vi) in Sodium Salt Solution

Electrochemical recovery of UO2 from LiCl-KCl-UO2F2 molten salt

Electrochemical Mix-Reduction Process of U and U-Fe Alloys on the Surface of Cathode in LiCl-KCl-U3O8 at 773K

Electrochemical and Thermodynamic Properties of Uranium on the Liquid Bismuth Electrode in LiCl-KCl Eutectic