Abstract:In this paper, TiC/Al 3 Ti/Al 2 O 3 composite nanoparticles were prepared using Ti, Al, and graphite powders, in a NaCl-KCl molten salt medium. The prepared powders were characterised by X-ray diffraction (XRD), scanning electron microscopy and energy dispersive spectroscopy (SEM-EDS), and X-ray photoelectron spectroscopy (XPS). The results showed that the one-step method could only directly generate the AlTi 2 C phase, but could not generate the TiC/Al 3 Ti/Al 2 O 3 phase. In the two-step method, the Al, Al 3 Ti, Al 2 Ti, and AlTi phases were used as precursors, and then the graphite powder was added. After sintering at 1000°C for 3 h, the TiC/Al 3 Ti/Al 2 O 3 composite nano-powder was successfully prepared, which can be used as the reinforcement of Al-based composites. During the synthesis process of the TiC/Al 3 Ti/Al 2 O 3 composite nano-powder, the intermediate AlTi 2 C phase was generated first, and the exposed [Ti] in the AlTi 2 C phase adsorbed C to generate the TiC phase. The formation of the TiC phase promoted the decomposition of the AlTi 2 C phase, resulting in the formation of the Al 3 Ti phase. Finally, the residual Al phase in the molten salt was oxidised to the Al 2 O 3 phase during the washing process. Dans cet article, on a préparé des nanoparticules composites de TiC/Al 3 Ti/Al 2 O 3 en utilisant des poudres de Ti, Al et de graphite, dans un milieu de sel fondu de NaCl-KCl. On a caractérisé les poudres préparées par diffraction des rayons x (DRX), microscopie électronique à balayage et spectroscopie à dispersion d'énergie (MEB-EDS) et spectroscopie de photoélectrons X (XPS). Les résultats ont montré que la méthode en une étape ne pouvait engendrer directement que la phase AlTi 2 C, mais ne pouvait pas engendrer la phase TiC/Al 3 Ti/Al 2 O 3 . Dans la méthode en deux étapes, on a utilisé les phases Al, Al 3 Ti, Al 2 Ti et AlTi comme précurseurs, et ensuite, on a ajouté la poudre de graphite. Après frittage à 1000°C pendant 3 h, on a préparé avec succès la nano-poudre composite TiC/Al 3 Ti/Al 2 O 3 , qui peut être utilisée comme le renforcement de composites à base d'Al. Pendant le procédé de synthèse de la nano-poudre composite TiC/Al 3 Ti/Al 2 O 3 , la phase intermédiaire AlTi 2 C a été engendrée en premier, et le [Ti] exposé dans la phase AlTi 2 C a adsorbé C pour engendrer la phase TiC. La formation de la phase TiC a favorisé la décomposition de la phase AlTi 2 C, amenant la formation de la phase Al 3 Ti. Finalement, la phase Al résiduelle dans le sel fondu a été oxydée en phase Al 2 O 3 pendant le procédé de lavage.

Fabrication of Al-Ti intermetallic alloy via aluminothermic reduction process from TiO2 in molten salts

A New Method for Preparing Titanium Aluminium Alloy Powder

Green preparation and synthesis mechanism of TiC/Al3Ti/Al2O3 composite nanoparticles

Electrochemical synthesis of Ti–Al–V alloy by chlorination of Ti2O3 and V2O3 in AlCl3-containing molten chloride salt

Experimental investigation on the formation mechanism of the TiFe alloy by the molten-salt electrolytic titanium concentrate

Precise fabrication of Ti2O from TiO2 by Al reduction towards potentially lower-cost Ti metal powder production

Composition and structure of Ti–Al alloy powders formed by electrochemical co-deposition in KCl–LiCl–MgCl2–TiCl3–AlCl3 molten salt

Fabrication of U-Ti alloy through direct electro-reduction from U3O8 and TiO2 mixtures in LiCl molten salt

In-Situ Precipitated Needle Like Nanocrystalline β-Ti Reinforced Porous Titanium Alloy via Molten Salt Electrolysis

Fabrication of CaAl12O19‐CaTiO3 composites and their potential usage for TiAl alloy smelting

Preparation of Ferrotitanium Alloy from Ilmenite by Electrochemical Reduction in Chloride Molten Salts

Preparation of Ferrotitanium from Ilmenite by Electrolysis-Assisted Calciothermic Reduction in CaCl2-NaCl Molten Salt

Facile synthesis of fine Ti–Al intermetallic compound powders via sodiothermic reduction in molten CaCl2

Direct electrochemical reduction of low titanium chlorides into titanium aluminide alloy powders from molten eutectic KCl–LiCl–MgCl2

Low-oxygen Ti-6Al-4V alloy powder synthesized by an aluminothermic reduction combined with deoxidation process

Thermodynamics of Aluminothermic Processes for Ferrotitanium Alloy Production from Bauxite Residue and Ilmenite

Mechanism of Melt Separation in Preparation of Low-Oxygen High Titanium Ferroalloy Prepared by Multistage and Deep Reduction

Novel method to achieve synergetic strength–ductility improvement of Al–Cu alloy by in situ TiC–TiB2 particles via direct reaction synthesis

Investigation on the reaction progress of titanium and lead chloride in NaCl-KCl melt

Electrodeposition of Titanium Aluminide (TiAl) Alloy from AlCl3–BMIC Ionic Liquid at Low Temperature

Ab initio molecular dynamics study on the local structures and solid/liquid interface in liquid Al-Ti and Al-B-Ti alloys