Abstract:In order to solve the problems (i.e. low infiltration efficiency, cracks, interface separation and poor mechanical properties) in the process of wood-derived C–SiC composites, the thermal modification of fir at low temperatures (300 °C ∼ 350 °C) combined with sol-gel infiltration was used to successfully produce biomorphic ceramics. The prepared materials were comprehensively characterized and exhibited improved interfacial bonding between C and SiC and mechanical properties. The weight gain per unit volume (0.123 g/cm 3 ) of SiO 2 gel in the fir thermally modified at 300 °C is 167.4%, higher than that (0.046 g/cm 3 ) of the unmodified fir. A well-bonded interface was formed between the SiO 2 gel and the pore wall of the fir thermally modified at 300 °C. With the increase of modification temperature from 300 °C to 350 °C, the distance between SiO 2 gel and the pore wall increases, and a gap (1–3 μm) is observed between SiO 2 gel and the pore wall of the fir carbonized at 600 °C. The C–SiC composites sintered at 1400 °C exhibited the highest compressive strength and bending strength of 40.8 ± 5.8 MPa and 11.7 ± 2.1 MPa, respectively, owing to the well-bonded interface between C of fir thermally modified at 300 °C and SiC. However, the composites sintered at 1600 °C for 120 min exhibited the lowest compressive strength and bending strength of 28.1 ± 13.4 MPa and 5.7 ± 1.6 MPa, respectively, which are 31.1% and 51.3% lower than those sintered at 1400 °C for 120 min, respectively. This might result from the porous structure formed by the excessive consumption of fir-derived carbon during the reaction between C and SiO 2 at 1600 °C for 120 min. Therefore, thermal modification in the preparation of biomorphic C–SiC composites can promote slurry infiltration and the formation of a well-bonded interface between C and SiC, thus improving the mechanical properties of the composites.

Low-temperature and efficient preparation of starfish-like Mo 2 C/C composites from waste biomass

High temperature in-situ synchrotron-based XRD study on the crystal structure evolution of C/C composite impregnated by FLiNaK molten salt

Waste biomass derived carbon supported Mo 2 C/C composite materials for heavy metal adsorption and hydrogen evolution reaction

Preparation method of C/C-SiC-MoSi2 ceramic-based composite material

Low-temperature selective synthesis of metastable α-MoC with electrochemical properties: Electrochemical co-reduction of CO2 and MoO3 in molten salts

A Powder Metallurgy Route to Fabricate CNT-reinforced Molybdenum-Hafnium-carbon Composites

Construction of three-dimensional mesh porous Mo 2 C/carbon composites by chitosan salting-out for efficient microwave absorption

Preparation of egg-structured ceramsites from molybdenum tailings with improved properties

Molten-salt treatment of waste biomass for preparation of carbon with enhanced capacitive properties and electrocatalytic activity towards oxygen reduction

Synthesis and characterization of submicro-sized V2AlC ceramics by a two-step modified molten salt method

Ablation properties of C/C-UHTCs and their preparation by reactive infiltration of K2MeF6 (Me = Zr, Ti) molten salt

Low-temperature thermally modified fir-derived biomorphic C–SiC composites prepared by sol-gel infiltration

In situ construction of ZIF-67 derived Mo2C@cobalt/carbon composites toward excellent electromagnetic wave absorption properties

Electrolytic synthesis of TiC/SiC nanocomposites from high titanium slag in molten salt

Synthesis of porous carbon-encapsulated Mo x C/Co based on NaCl template and ZIF-67 towards enhancing electromagnetic wave absorption

Molten salts synthesis of Mo 2 C nanoflake and its composites for enhanced lithium-storage performance

Influence of (Ta Nb Ti V) C powders synthesized by molten salt at low temperature on densification and properties of high entropy carbide ceramics

Preparation and mechanical behaviors of multiscale SiC nanowires/carbon fiber reinforced silicon oxycarbide ceramic composites

Low temperature fabrication of Cf/BNi/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiCm high entropy ceramic matrix composite by slurry coating and laminating combined with precursor infiltration and pyrolysis

Composite ceramic fiber and preparation method thereof

Co/P co-doped bamboo-based woodceramics with a sandwich structure modified by carbon nanotube electrodeposition as supercapacitor electrodes